LUVOCOM®50/TF/15/NAT is a polycarbonate (PC) material,. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,. LUVOCOM®The main features of 50/TF/15/NAT are: flame retardant/rated flame Good dimensional stability Impact resistance Wear-resistant Heat resistance Typical application areas include: engineering/industrial accessories Electrical/electronic applications business/office supplies Sporting goods medical/health care

General Information
Additive	PTFE lubricant (15%)
Features	Good dimensional stability Low friction coefficient Impact resistance, good Good liquidity Good wear resistance Heat resistance, high Lubrication
Uses	Plug Gear Engineering accessories Switch Business equipment Sporting goods Medical/nursing supplies
Appearance	Natural color

Physical	Nominal Value	Unit	Test Method
Density	1.30	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (300°C/5.0 kg)	55	g/10 min	ISO 1133
Melt Volume-Flow Rate (MVR) (300°C/5.0 kg)	50.0	cm³/10min	ISO 1133
Molding Shrinkage	0.60 - 0.80	%	DIN 16901
Water Absorption (23°C, 24 hr)	< 0.20	%

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	2700	MPa	ISO 527-2
Tensile Stress (Break)	55.0	MPa	ISO 527-2
Tensile Strain (Yield)	5.0	%	ISO 527-2
Flexural Modulus	2200	MPa	ISO 178
Flexural Stress	75.0	MPa	ISO 178
Flexural Strain at Flexural Strength	6.5	%	ISO 178

Thermal	Nominal Value	Unit	Test Method
Maximum operating temperature- Short Term	150	°C

Electrical	Nominal Value	Unit	Test Method
Insulation Resistance	> 1.0E+12	ohms	IEC 60167

Impact	Nominal Value	Unit	Test Method
Charpy Unnotched Impact Strength (23°C)	120	kJ/m²	ISO 179/1eU

Thermal	Nominal Value	Unit	Test Method
Continuous Use Temperature	130	°C	UL 746B
Vicat Softening Temperature	160	°C	ISO 306/A
CLTE - Flow	7.0E-5	cm/cm/°C	DIN 53752
Thermal Conductivity	0.20	W/m/K	DIN 52612

Flammability	Nominal Value	Unit	Test Method
Flame Rating ¹	V-0		UL 94

Injection	Nominal Value	Unit
Drying Temperature - Desiccant Dryer	120	°C
Drying Time - Desiccant Dryer	4.0 - 6.0	hr
Rear Temperature	280 - 300	°C
Middle Temperature	290 - 310	°C
Front Temperature	300 - 320	°C
Nozzle Temperature	290 - 310	°C
Processing (Melt) Temp	295	°C
Mold Temperature	80 - 120	°C

Injection instructions
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing, the moisture level should not exceed 0.02%, otherwise molecular degradation may occur. Suitable heat treatment may increase resistance to the formation of stress cracks. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Injection instructions

General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing, the moisture level should not exceed 0.02%, otherwise molecular degradation may occur. Suitable heat treatment may increase resistance to the formation of stress cracks. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Note Message
1 .	Not recognized by UL.

Category:	PC , Polycarbonate
Manufacturer:	LEHVOSS Group
Trademark:	LUVOCOM®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	mt8LX5_LUVOCOM50TF15NAT.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Sindustris PP HM5205	Sincerity Australia Pty Ltd.	PP, Unspecified	Sindustris PP
Ad-Tech Epoxy CER-112-2	Ad-Tech Plastic Systems Corp.	Epoxy	Ad-Tech Epoxy
Extir® CM Galileo Europa 5	Versalis S.p.A.	PS (EPS)	Extir®
ESTADIENE 0417 GF	Cossa Polimeri S.r.l.	ABS	ESTADIENE
Hanwha Total PP NH53G	HANWHA TOTAL PETROCHEMICALS Co., Ltd.	PP, High Crystal	Hanwha Total PP