Quadrant EPP Delrin® Acetal
| Category: | Acetal (POM) Homopolymer , Acetal (POM) Homopolymer |
| Manufacturer: | Quadrant Engineering Plastic Products |
| Trademark: | Quadrant EPP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mstbvC_Quadrant-EPP-Delrin-Acetal.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Delrin* is a homopolymer acetal. Stocked in rod and plate, it offers slightly higher mechanical properties than Acetron GP Acetal, but may contain a low-density center, especially in larger cross-sections. Delrin is ideal for small diameter, thin-walled bushings that benefit from the additional strength and hardness of homopolymer acetal. Data provided by Quadrant Engineering Plastic Products from tests on stock shapes and parts produced by Quadrant EPP. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.41 | g/cm³ | ASTM D792 |
| Water Absorption | ASTM D570 | ||
| 24 hr | 0.20 | % | |
| Saturation | 0.90 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| M-Scale | 89 | ||
| R-Scale | 122 | ||
| Durometer Hardness (Shore D) | 86 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3100 | MPa | ASTM D638 |
| Tensile Strength (Ultimate) | 75.8 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 30 | % | ASTM D638 |
| Flexural Modulus | 3100 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 89.6 | MPa | ASTM D790 |
| Compressive Modulus | 3100 | MPa | ASTM D695 |
| Compressive Strength (10% Strain) | 110 | MPa | ASTM D695 |
| Shear Strength | 62.1 | MPa | ASTM D732 |
| Coefficient of Friction (vs. Steel - Static) | 0.25 | Internal Method | |
| Wear Factor | 400 | 10^-8 mm³/N·m | ASTM D3702 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 53 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 121 | °C | ASTM D648 |
| Maximum Use Temperature - Long Term, Air | 82 | °C |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Limiting Pressure Velocity 1 | 0.0946 | MPa·m/s | Internal Method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Crystallization Temperature (DSC) | 175 | °C | ASTM D3418 |
| CLTE - Flow 2(-40 to 149°C) | 8.5E-5 | cm/cm/°C | ASTM E831 |
| Thermal Conductivity | 0.36 | W/m/K | ASTM F433 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity 3 | > 1.0E+13 | ohms | Internal Method |
| Dielectric Strength 4 | 18 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.70 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 5.0E-3 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.18 mm, Estimated Rating) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 4:1 safety factor |
| 2 . | 68°F |
| 3 . | EOS/ESD S11.11 |
| 4 . | Method A (Short-Time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC V961 BLK580 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Gallonprene® GP410-8003 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| ELASTOSIL® LR 3001/55 FR A/B | Wacker Chemie AG | Silicone | ELASTOSIL® LR |
| ENFLEX S4065A CL NAT | ENPLAST Americas, a Ravago Group Company | TPE | ENFLEX |
| Karina CLEAR PVC COMPOUND 65/200-SD | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |