TEKAFIN™ P730G10
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Mando Advanced Materials Co., Ltd. |
| Trademark: | TEKAFIN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ms9PFf_TEKAFIN-P730G10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TEKAFIN P730G10 is Compounded-PP GF 10% high strength product. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.968 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.20 to 0.90 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break) | 53.9 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 5.0 | % | ASTM D638 |
| Flexural Modulus 3 | 2550 | MPa | ASTM D790 |
| Flexural Strength 4 | 78.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 59 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 160 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 to 80.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Rear Temperature | 190 to 210 | °C | |
| Middle Temperature | 200 to 230 | °C | |
| Front Temperature | 200 to 230 | °C | |
| Nozzle Temperature | 210 to 230 | °C | |
| Processing (Melt) Temp | 210 to 230 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 3.0 mm/min |
| 4 . | 3.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL® C 52G4 MZ25 GREY R7035 | Solvay Engineering Plastics | Nylon 6 | TECHNYL® C |
| Sylvin 2940-60 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| TRIBOFORCE® PA66 C0200 | LEIS Polytechnik - polymere Werkstoffe GmbH | Nylon 66 | TRIBOFORCE® |
| Cheng Yu NG1150S | Cheng Yu Plastic Company Limited | Nylon 66 | Cheng Yu |
| Epoxies, Ect. 20-3068 (CAT.1) | Epoxies, Etc. | Epoxy | Epoxies, Ect. |