AFFINITY™ PL 1850G
| Category: | POP , Polyolefin Plastomer |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | AFFINITY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ms24en_AFFINITY-PL-1850G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
AFFINITY* PL 1850G Polyolefin Plastomer (POP) is produced via INSITE* Technology. It is designed to provide blown and cast film products with low temperature sealability, excellent optics and good abuse resistance. It has value as a sealant layer in multilayer film structures for dry and liquid packaging.
Complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.902 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 3.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 20 | µm | |
| Film Puncture Energy (20 µm) | 4.28 | J | Internal method |
| Film Puncture Force (20 µm) | 47.6 | N | Internal method |
| Film Puncture Resistance (20 µm) | 31.4 | J/cm³ | Internal method |
| secant modulus | ASTM D882 | ||
| 2% secant, MD : 20 µm | 108 | MPa | ASTM D882 |
| 2% secant, TD : 20 µm | 115 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 20 µm | 9.93 | MPa | ASTM D882 |
| TD : Yield, 20 µm | 5.45 | MPa | ASTM D882 |
| MD : Break, 20 µm | 44.6 | MPa | ASTM D882 |
| TD : Break, 20 µm | 29.8 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 20 µm | 350 | % | ASTM D882 |
| TD : Break, 20 µm | 570 | % | ASTM D882 |
| Dart Drop Impact (20 µm) | > 830 | g | ASTM D1709B |
| Elmendorf Tear Strength 1 | ASTM D1922 | ||
| MD : 20 µm | 120 | g | ASTM D1922 |
| TD : 20 µm | 410 | g | ASTM D1922 |
| Seal Initiation Temperature 2(20 µm) | 93.9 | °C | Internal method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 85.0 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 98.0 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (20°, 20.3 µm) | 144 | ASTM D2457 | |
| Haze (20.3 µm) | 0.70 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 274 | °C |
| Extrusion instructions |
|---|
| 铸造薄膜的制造条件： 螺杆尺寸：3.5 英寸 (89 mm)；32:1 L/D 螺杆速度：10 rpm 螺杆尺寸：2.5 英寸 (63.5 mm)；24:1 L/D 螺杆速度：27 rpm 螺杆尺寸：2.0 英寸 (51 mm)；24:1 L/D 螺杆速度：46 rpm 螺杆类型：Sterlex，带 Maddock Mixer 的单跨型和单跨型 模具间隙：20 密尔 (0.5 mm) 冷却辊温度：70°F (21°C) 熔体温度：525°F (274°C) 输出：243 磅/小时 生产线速度：600 fpm（183 米/分） |
| Note Message | |
|---|---|
| 1 . | Modified rectangular test piece. |
| 2 . | Achieve a temperature of 1 psig (4.4 N/25.4mm) heat seal strength. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Xuchuan XCY-5590 | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Baytec® 352 (82A) | Covestro - PUR | TSU | Baytec® |
| Anjaconduct® 350-KF1E3 | Almaak International GmbH | Nylon 66 | Anjaconduct® |
| Delta IPP 2508 | Delta Polymers | PP Copolymer | Delta |
| PENTAMID B GK20 H UV black | PENTAC Polymer GmbH | Nylon 6 | PENTAMID B |