PULSE™ 630GF
| Category: | PC+ABS , PC/ABS Engineering Resin |
| Manufacturer: | Trinseo |
| Trademark: | PULSE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mpnbH3_PULSE-630GF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PULSE 630GF is a 13% glass filled PC/ABS resin, available in standard black. It combines very high stiffness, low CLTE, excellent processability, good foam adhesion and long term heat stability. Its thermal resistance allows parts to meet the most severe sunload and temperature conditions in car interiors. The resin also allows for excellent post operations like stamping, transportation and stacking. Scrap generation during post processing is significantly below the levels obtained with glass filled SMA. To ensure low carbon emission characteristics and high thermal stability this product is based on the Company's unique mass ABS technology. PULSE 630GF is especially suitable for instrument panel retainers which are to be foamed, air ducts etc. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.17 | g/cm³ | ISO 1183/B |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 19 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.30 to 0.40 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4700 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 82.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 2.8 | % | |
| Break | 3.3 | % | |
| Flexural Modulus 1 | 4700 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | 35 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength (23°C) | 9.0 | kJ/m² | ISO 180/4A |
| Multi-Axial Instrumented Impact Energy (23°C, Total Penetration Energy) | 8.00 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 122 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 113 | °C | ISO 75-2/A |
| CLTE | ASTM D696 | ||
| Flow : -30 to 80°C | 3.5E-5 | cm/cm/°C | |
| Transverse : -30 to 80°C | 6.0E-5 | cm/cm/°C |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Carbon Emission | 10.0 | µg/g | VDA 277 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VENELENE® 11PG4 | Poliolefinas Internacionales, C.A. (Polinter) | LLDPE | VENELENE® |
| ALTECH® PA66 A 4240/500 GF15 MR25 | ALBIS PLASTIC GmbH | Nylon 66 | ALTECH® PA66 |
| Aurora PVC AP2144 Series 050902 | Aurora Plastics, Inc. | PVC, Unspecified | Aurora PVC |
| HAIPLEN H50 C4 | Taro Plast S.p.A. | PP Homopolymer | HAIPLEN |
| EPO-TEK® H20E-SLR-HVMX | Epoxy Technology Inc. | Epoxy | EPO-TEK® |