Badamid® B70 GK30
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Bada AG |
| Trademark: | Badamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mpKS4t_Badamid-B70-GK30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% glass beads reinforced injection moulding grade with superior mechanical properties and high dimensional stability |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.32 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 7.0 | -- | % | |
| Equilibrium, 23°C, 50% RH | 2.1 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 4500 | 1900 | MPa | ISO 527-2/1 |
| Tensile Stress 1(Break, 23°C) | 80.0 | 55.0 | MPa | ISO 527-2/5 |
| Tensile Strain 2(Break, 23°C) | 8.0 | 12 | % | ISO 527-2/5 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength 3 | ISO 179/1eA | |||
| -30°C | 5.0 | 6.0 | kJ/m² | |
| 23°C | 5.0 | 11 | kJ/m² | |
| Charpy Unnotched Impact Strength 4 | ISO 179/1eU | |||
| -30°C | 35 | 55 | kJ/m² | |
| 23°C | 45 | 70 | kJ/m² | |
| Notched Izod Impact Strength 5 | ISO 180/1A | |||
| -30°C | 5.0 | 5.0 | kJ/m² | |
| 23°C | 5.0 | 9.0 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature 6 | ||||
| 0.45 MPa, Unannealed | 180 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 90.0 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) 7 | 222 | -- | °C | ISO 3146 |
| Maximum Service Temperature | IEC 216 | |||
| 20000 hrs | 100 | -- | °C | |
| some hours | 195 | -- | °C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity 8 | 1.0E+12 | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity 9 | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Relative Permittivity 10(1 MHz) | 3.70 | 6.10 | IEC 60250 | |
| Dissipation Factor 11(1 MHz) | 0.022 | 0.21 | IEC 60250 | |
| Comparative Tracking Index | 500 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.800 mm | HB | -- | ||
| 1.60 mm | HB | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 260 to 280 | °C | |
| Mold Temperature | 80.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | Test Specimen accordng to ISO 3167, Type A |
| 2 . | Test Specimen accordng to ISO 3167, Type A |
| 3 . | 80x10x4 mm |
| 4 . | 80x10x4 mm |
| 5 . | 80x10x4 mm |
| 6 . | 110x10x4mm |
| 7 . | 10 K/min, Compounded for moulding |
| 8 . | 80x80x1 mm |
| 9 . | 80x80x1 mm |
| 10 . | 80x80x1 mm |
| 11 . | 80x80x1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PP 5201L | SABIC Americas, Inc. | PP Homopolymer | SABIC® PP |
| Tecomid® NB40 NL FY70 | Eurotec Engineering Plastics | Nylon 6 | Tecomid® |
| TangoBlackPlus™ FLX980 | Stratasys | Unspecified | TangoBlackPlus™ |
| NEXUS Reprocessed PPC 30/2 RBK | Nexus Resin Group, LLC. | PP Copolymer | NEXUS Reprocessed |
| Cri-Line SP-715-THK | Cri-Tech, Inc. | Fluorelastomer | Cri-Line |