Order Products : sales@su-jiao.com
Corton® 1009 HS NATURAL
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | PolyPacific Pty. Ltd. |
| Trademark: | Corton® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mpFg7Z_Corton-1009-HS-NATURAL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| CORTON 1009 HS Natural is a 20% talc filled polypropylene compound. It is a high flow injection moulding grade developed for rigid components and stabilized to meet automotive heat ageing requirements of 1000 hours at 150°C and 48 hours at 150°C in contact with copper. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 21 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.00 mm) | 1.1 to 1.3 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 3.00 mm) | 101 | ASTM D785 | |
| Durometer Hardness | ASTM D2240 | ||
| Shore D, 3.00 mm | 77 | ||
| Shore D, 15 sec, 3.00 mm | 70 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.00 mm) | 33.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.00 mm) | 30 | % | ASTM D638 |
| Flexural Modulus (3.00 mm) | 2880 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.00 mm) | 26 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.00 mm) | 380 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.00 mm | 128 | °C | |
| 1.8 MPa, Unannealed, 3.00 mm | 72.0 | °C | |
| CLTE - Flow (-30 to 30°C, 3.00 mm) | 8.0E-5 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 120 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Regrind | 10 | % | |
| Processing (Melt) Temp | 200 to 260 | °C | |
| Mold Temperature | 20.0 to 60.0 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 289 F | RTP Company | Nylon 12 | RTP |
| Sindustris PBT GP2157FT | Sincerity Australia Pty Ltd. | PBT | Sindustris PBT |
| Topolymer® 5111-951E | Dongguan Top Polymer Enterprise | TPE | Topolymer® |
| Petrothene® XL07426X01 | LyondellBasell Industries | Polyolefin, Unspecified | Petrothene® |
| Kinta R4-002 BK | Kinta Technology (Hong Kong) Co., Ltd. | PPS | Kinta |