Shinko-Lac® ABS VP-2
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Mitsubishi Rayon America Inc. |
| Trademark: | Shinko-Lac® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | moYb2q_Shinko-Lac-ABS-VP-2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Shinko-Lac ABS VP-2 is a flame retardant grade that offers excellent flame retardant characteristics to products along with good thermal stability. Good flow property offers easy processing especially for large and thin products. Typical applications of VP-2 include copy machine housings. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.21 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 8.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.21 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 104 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2350 | MPa | ASTM D638 |
| Tensile Strength (Yield, 23°C) | 40.2 | MPa | ASTM D638 |
| Flexural Modulus (23°C, 6.35 mm) | 2400 | MPa | ASTM D790 |
| Flexural Strength (Yield, 23°C, 6.35 mm) | 60.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 6.35 mm) | 140 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 12.7 mm) | 84.0 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.18 mm, NC) | V-1 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 90.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 200 - 250 | °C | |
| Middle Temperature | 200 - 250 | °C | |
| Front Temperature | 200 - 250 | °C | |
| Mold Temperature | 40.0 - 80.0 | °C | |
| Injection Pressure | 68.6 - 108 | MPa |
| Injection instructions |
|---|
| Higher mold temperature provides a product with excellent surface finish and less residual stress. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 600 FR AU | RTP Company | ABS | RTP |
| PRL PPX-EN-FR3 | Polymer Resources Ltd. | PPE+PS | PRL |
| Wellamid® XT1482-BK | Wellman Engineering Resins | Nylon 66 | Wellamid® |
| Mylar® J (650 guage) | DuPont Teijin Films U.S. | PET | Mylar® |
| Karina CLEAR PVC COMPOUND -E 57/200-D-AT-IS-SD | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |