Order Products : sales@su-jiao.com
Nypol® PA A3 G35 NTLA010 NR451
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Petropol Industry and Trade of Polymers LTDA |
| Trademark: | Nypol® PA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | moDy2y_Nypol-PA-A3-G35-NTLA010-NR451.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 6.6 natural reinforced with 35% fiberglass, good set of thermal and mechanical properties. Ideal for injection molding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.41 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.50 | -- | % | ASTM D955 |
| Water Absorption | ASTM D570 | |||
| Saturation | 5.3 | -- | % | |
| Equilibrium | 1.7 | -- | % | |
| Ash Content | 33 to 37 | -- | % | ASTM D2584 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness | 280 | 210 | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (1°C) | 11500 | 8900 | MPa | ASTM D638 |
| Tensile Strength 1 | 210 | 155 | MPa | ASTM D638 |
| Tensile Elongation (Break, 5°C) | 3.2 | 4.0 | % | ASTM D638 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 15 | 17 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 98 | 110 | kJ/m² | ISO 179 |
| Notched Izod Impact (Area) (23°C) | 14.0 | 18.0 | kJ/m² | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 254 | -- | °C | ASTM D648 |
| Vicat Softening Temperature | 256 | -- | °C | ISO 306/B |
| CLTE | ASTM E831 | |||
| Flow | 2.0E-5 | -- | cm/cm/°C | |
| Transverse | 1.0E-4 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+12 | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Dissipation Factor (1 MHz) | 0.020 | 0.15 | IEC 60250 | |
| Comparative Tracking Index | 550 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (0.700 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 80.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Polypropylene GC30P100-00 | RheTech, Inc. | PP, Unspecified | RheTech Polypropylene |
| Shin-Etsu Elastomer KE-971U | Shin-Etsu Silicones of America | Silicone Rubber, HTV | Shin-Etsu Elastomer |
| SLOVAMID® 6 GF 35 | Plastcom | Nylon 6 | SLOVAMID® 6 |
| Topilene® J742 | Hyosung Corporation | PP Impact Copolymer | Topilene® |
| Karina WHITE PVC COMPOUND 800D10/1-A-AT-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |