LNP™ THERMOCOMP™ LX03447 compound
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mnWsGT_LNP-THERMOCOMP-LX03447-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP LX03447 is a compound based on Polyetheretherketone containing Proprietary Filler(s). Also known as: LNP* THERMOCOMP* Compound PDX-L-03447 Product reorder name: LX03447 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.43 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.10 to 3.0 | % | |
| Across Flow : 24 hr | 0.70 to 0.90 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.050 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.070 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 28500 | MPa | ASTM D638 |
| -- | 28400 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 248 | MPa | ASTM D638 |
| Break | 246 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 1.6 | % | ASTM D638 |
| Break | 1.5 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 23700 | MPa | ASTM D790 |
| -- 5 | 23800 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 360 | MPa | ISO 178 |
| Yield, 50.0 mm Span 6 | 370 | MPa | ASTM D790 |
| Break, 50.0 mm Span 7 | 365 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 70 | J/m | ASTM D256 |
| 23°C 8 | 6.1 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 770 | J/m | ASTM D4812 |
| 23°C 9 | 46 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 7.00 | J | ASTM D3763 |
| -- | 3.00 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 337 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 10 | 335 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 325 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 11 | 318 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 9.0E-6 | cm/cm/°C | |
| Transverse : -30 to 30°C | 3.9E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Rear Temperature | 370 to 380 | °C | |
| Middle Temperature | 380 to 400 | °C | |
| Front Temperature | 380 to 400 | °C | |
| Mold Temperature | 175 to 190 | °C | |
| Back Pressure | 0.300 to 0.700 | MPa | |
| Screw Speed | 60 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| 11 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Therma-Tech™ X TT3300-8704 EI FR | PolyOne Corporation | PBT | Therma-Tech™ |
| Chemlon® A30 | Teknor Apex Company (Chem Polymer) | Nylon 66 | Chemlon® |
| Generic PC+Polyester - Glass Fiber | Generic | PC+Polyester | Generic |
| Perlast® G74S | Precision Polymer Engineering Ltd. | Perfluoroelastomer | Perlast® |
| LNP™ LUBRILOY™ RF208 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRILOY™ |