CYCOLAC™ GX3800F resin
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | CYCOLAC™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mmRcH5_CYCOLAC-GX3800F-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High impact ABS for sheet extrusion and blow molding applications. FDA food contact compliant. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.03 | g/cm³ | ASTM D792 |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 4.20 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.60 - 0.80 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2080 | MPa | ASTM D638 |
| Tensile Strength 2 | ASTM D638 | ||
| Yield | 40.0 | MPa | ASTM D638 |
| Fracture | 30.3 | MPa | ASTM D638 |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield | 3.1 | % | ASTM D638 |
| Fracture | 32 | % | ASTM D638 |
| Flexural Modulus 4(50.0 mm Span) | 2160 | MPa | ASTM D790 |
| Flexural Strength 5(Yield, 50.0 mm Span) | 66.9 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C | 300 | J/m | ASTM D256 |
| 23°C | 430 | J/m | ASTM D256 |
| Instrumented Dart Impact (23°C, Total Energy) | 50.8 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.20mm | 93.3 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 80.6 | °C | ASTM D648 |
| Vicat Softening Temperature | 107 | °C | ASTM D1525 6 |
| Linear thermal expansion coefficient | ASTM E831 | ||
| Flow : -40 to 40°C | 1.0E-4 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 1.0E-4 | cm/cm/°C | ASTM E831 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (240°C, 100 sec^-1) | 1400 | Pa·s | ASTM D3835 |
| Extrusion instructions |
|---|
| Extrusion Blow Molding Parameters: Adapter - Zone 5 Temperature: 210 - 232 °C Barrel - Zone 1 Temperature: 204 - 227 °C Barrel - Zone 2 Temperature: 204 - 227 °C Barrel - Zone 3 Temperature: 204 - 227 °C Barrel - Zone 4 Temperature: 204 - 227 °C Die Temperature: 216 - 235 °C Drying Temperature: 82 - 88 °C Drying Time: 4 - 5 hrs Drying Time (Cumulative): 24 hrs Extruder Feed Zone Temperature: 60 - 77 °C Head - Zone 6 - Top Temperature: 216 - 232 °C Head - Zone 7 - Bottom Temperature: 216 - 232 °C Maximum Moisture Content: 0.02 % Melt Temperature (Parison): 216 - 232 °C Mold Temperature: 38 - 82 °C Screw Speed: 20 - 60 rpm Sheet Extrusion Parameters: Adapter Temperature: 204 - 249 °C Barrel - Zone 1 Temperature: 171 - 199 °C Barrel - Zone 2 Temperature: 182 - 221 °C Barrel - Zone 3 Temperature: 188 - 227 °C Barrel - Zone 4 Temperature: 199 - 238 °C Die Temperature: 204 - 249 °C Drying Temperature: 82 - 93 °C Drying Time: 4 hrs Maximum Moisture Content: 0.02 % Melt Temperature: 216 - 260 °C Roll Stack Temp - Bottom: 99 - 104 °C Roll Stack Temp - Middle: 93 - 104 °C Roll Stack Temp - Top: 88 - 93 °C |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom M60450 | Spartech Polycom | PVC, Unspecified | Spartech |
| Sylvin 9067-95 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| API PS 550 | American Polymers, Inc. | PS (HIPS) | API PS |
| Fainplast PVC CKL 0222 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Lucent PC PC/ABS-1216LG | Lucent Polymers, Inc. | PC+ABS | Lucent PC |