LNP™ THERMOCOMP™ LF002XXP-WT02005 compound
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mmG7k6_LNP-THERMOCOMP-LF002XXP-WT02005-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* THERMOCOMP* LF002XXP-WT02005 is a compound based on Polyetheretherketone resin contaninig Glass Fiber. Added Features include: custom color. Also known as: LNP* THERMOCOMP* Compound LF-1002 WT-020-05 Product reorder name: LF002XXP-WT02005 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.88 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.40 to 0.60 | % | Internal Method |
| Water Absorption (23°C, 24 hr) | 0.040 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8550 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 110 | MPa | ISO 527-2/5 |
| Tensile Strain (Yield) | 2.6 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 7500 | MPa | ISO 178 |
| Flexural Stress | 170 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 2(23°C) | 5.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 3(23°C) | 30 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4(1.8 MPa, Unannealed, 64.0 mm Span) | 179 | °C | ISO 75-2/Af |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 2.8E-5 | cm/cm/°C | |
| Transverse : 23 to 60°C | 4.2E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 to 149 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 349 to 360 | °C | |
| Middle Temperature | 366 to 377 | °C | |
| Front Temperature | 382 to 393 | °C | |
| Processing (Melt) Temp | 382 to 388 | °C | |
| Mold Temperature | 138 to 166 | °C | |
| Back Pressure | 0.344 to 0.689 | MPa | |
| Screw Speed | 60 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PROTEQ™ ES880 | Qenos Pty Ltd | PP, Unspecified | PROTEQ™ |
| New-prene™ 9345N | Total Polymer Vision (Suzhou) Co., LTD | SEBS | New-prene™ |
| Ebalta LH 22 / GL | Ebalta Kunststoff GmbH | Epoxy | Ebalta |
| LUVOCOM® 1-8385 | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |
| Thermec N™ 4314R45H | Technical Polymers, LLC | PPA | Thermec N™ |