LNP™ STAT-KON™ DE002 compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mm3n6Z_LNP-STAT-KON-DE002-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* STAT-KON* DE002 is a Polycarbonate base resin containing 10% Carbon Fiber. Added feature of this grade is: Electrically Conductive. Also known as: LNP* STAT-KON* Compound DC-1002 Product reorder name: DE002 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.29 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.20 to 0.40 | % | |
| Across Flow : 24 hr | 0.40 to 0.60 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.080 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.080 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 11100 | MPa | ASTM D638 |
| -- | 10300 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 97.0 | MPa | ASTM D638 |
| Break | 97.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 7.5 | % | ASTM D638 |
| Break | 7.3 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 7460 | MPa | ASTM D790 |
| -- 5 | 7440 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 149 | MPa | ISO 178 |
| Break, 50.0 mm Span 6 | 158 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 85 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 690 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 146 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 7 | 145 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 141 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 8 | 142 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 2.6E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 5.8E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 3.0 to 5.0 | ohms | ASTM D257 |
| Volume Resistivity | 4.0 to 6.0 | ohms·cm | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 to 304 | °C | |
| Middle Temperature | 310 to 321 | °C | |
| Front Temperature | 321 to 332 | °C | |
| Processing (Melt) Temp | 304 to 327 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 mm |
| 8 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® HDPE B4406 | Saudi Basic Industries Corporation (SABIC) | HDPE | SABIC® HDPE |
| SolVin 271DF | INOVYN | PVC, Unspecified | SolVin |
| Double Elephant SX-304 | Suzhou Double Elephant Optical Material Co., LTD. | Acrylic (PMMA) | Double Elephant |
| INEOS PP 100-GA09 | INEOS Olefins & Polymers Europe | PP Homopolymer | INEOS PP |
| Pibiflex® E4482 NATURALE | SO.F.TER. SPA | TPC-ET | Pibiflex® |