Latiohm 62-03 PD01 G/20
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Latiohm |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mkixNu_Latiohm-62-03-PD01-G-20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Partially conductive/dissipative compound based on Polyamide 6 (PA 6). Glass fibres. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.35 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.65 to 0.95 | % | |
| Flow : 2.00 mm | 0.30 to 0.55 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 15500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 200 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 2.5 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 9.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 65 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C, 3.20 mm) | 100 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 220 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 210 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 215 | °C | ISO 306/B50 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+3 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+3 | ohms·cm | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 100 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 240 to 280 | °C | |
| Mold Temperature | 80.0 to 100 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | at 60 Mpa of cavity pressure |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RANPELEN SFI-841 | Lotte Chemical Corporation | PP Terpolymer | RANPELEN |
| Witcom PC 6C-3L1 | Witcom Engineering Plastics B.V. | PC | Witcom PC |
| YUCLAIR® JG910 | SK Global Chemical | HDPE | YUCLAIR® |
| Hostacom ERC 487N C12827 | LyondellBasell Industries | PP Copolymer | Hostacom |
| Axiall PVC 19781 | Axiall Corporation | PVC, Flexible | Axiall PVC |