Order Products : sales@su-jiao.com
LG MABS TR580
| Category: | MABS , Methyl Methacrylate / ABS |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | LG MABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mkiEvp_LGMABSTR580.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Description
Application
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 2.5 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 - 0.70 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 39.2 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 30 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 1770 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 63.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| 23°C, 3.20 mm | 78 | J/m | ASTM D256 |
| 23°C, 6.40 mm | 78 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 79.0 | °C | ASTM D648 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance | 90.0 | % | ASTM D1003 |
| Haze | 1.2 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80 - 90 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 210 - 230 | °C | |
| Middle Temperature | 220 - 240 | °C | |
| Front Temperature | 230 - 250 | °C | |
| Nozzle Temperature | 230 - 260 | °C | |
| Processing (Melt) Temp | 220 - 250 | °C | |
| Mold Temperature | 50 - 70 | °C | |
| Back Pressure | 29.4 - 58.8 | MPa | |
| Screw Speed | < 80 | rpm |
| Injection instructions |
|---|
| Minimum Moisture Content: 0.01% |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 15 mm/min |
| 4 . | 15 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Clearflex® FG 308 | Versalis S.p.A. | LLDPE | Clearflex® |
| Gallonprene® GP210-8504 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Geon™ Vinyl Rigid Extrusion L7703 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Extrusion |
| Hifax X M1 T05 | LyondellBasell Industries | PP Copolymer | Hifax |
| Karina IVORY PVC COMPOUND -E 854-35/ 9-A-ERYB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |