Badalac® ABS 20 GF15
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Bada AG |
| Trademark: | Badalac® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mkUSnV_Badalac-ABS-20-GF15.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Easy flowing, 15% glass fibres reinforced standard injection moulding grade |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.10 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 10.0 | cm³/10min | ISO 1133 |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.90 | % | |
| Equilibrium, 23°C, 50% RH | 0.20 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1(23°C) | 6000 | MPa | ISO 527-2/1 |
| Tensile Stress 2(Break, 23°C) | 85.0 | MPa | ISO 527-2/5 |
| Tensile Strain 3(Break, 23°C) | 2.0 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 4 | ISO 179/1eA | ||
| -30°C | 4.0 | kJ/m² | |
| 23°C | 5.0 | kJ/m² | |
| Charpy Unnotched Impact Strength 5 | ISO 179/1eU | ||
| -30°C | 20 | kJ/m² | |
| 23°C | 25 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 6 | |||
| 0.45 MPa, Unannealed | 115 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 110 | °C | ISO 75-2/A |
| Vicat Softening Temperature 7 | |||
| -- | 116 | °C | ISO 306/A50 |
| -- | 114 | °C | ISO 306/B50 |
| Maximum Service Temperature - 20000 hrs | 85 | °C | IEC 216 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity 8 | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity 9 | 1.0E+13 | ohms·cm | IEC 60093 |
| Electric Strength 10 | 37 | kV/mm | IEC 60243-1 |
| Relative Permittivity 11(1 MHz) | 2.80 | IEC 60250 | |
| Dissipation Factor 12(1 MHz) | 7.9E-3 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating 13(0.800 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 220 to 260 | °C | |
| Mold Temperature | 30.0 to 60.0 | °C |
| Note Message | |
|---|---|
| 1 . | Test Specimen accordng to ISO 3167, Type A |
| 2 . | Test Specimen accordng to ISO 3167, Type A |
| 3 . | Test Specimen accordng to ISO 3167, Type A |
| 4 . | 80x10x4 mm |
| 5 . | 80x10x4 mm |
| 6 . | 110x10x4 mm |
| 7 . | Compound for moulding |
| 8 . | 80x80x1 mm |
| 9 . | 80x80x1 mm |
| 10 . | 80x80x1 mm |
| 11 . | 80x80x1 mm |
| 12 . | 80x80x1 mm |
| 13 . | 125x13x0.8 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RELENE® 24FS040 | Reliance Industries Limited | LDPE | RELENE® |
| SABIC® STAMAX 30YM240E | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® STAMAX |
| TORZEN® U4632HSL BKB01 | INVISTA Engineering Polymers | Nylon 66 | TORZEN® |
| Andur 95-AP/Curene® 185 | Anderson Development Company | PUR-Ether/TDI | Andur |
| Geon™ Vinyl Flexible A5DM0 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |