ALTECH® PA66 B 2030/209 GF30
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | ALBIS PLASTIC GmbH |
| Trademark: | ALTECH® PA66 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mkTK9a_ALTECH-PA66-B-2030-209-GF30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ALTECH® PA66 B 2030/209 GF30 is a Polyamide 66 (Nylon 66) product filled with 30% glass fiber. It can be processed by injection molding and is available in Asia Pacific, Europe, or North America. Typical application: Automotive. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.36 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 5.5 | -- | % | |
| Equilibrium, 23°C, 50% RH | 1.7 | -- | % | |
| Viscosity Number 1(96% H2SO4 (Sulphuric Acid)) | 140 | -- | cm³/g | ISO 307 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 9000 | -- | MPa | ISO 527-2 |
| Tensile Stress (Break) | 165 | -- | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 | -- | % | ISO 527-2 |
| Flexural Modulus | 8500 | -- | MPa | ISO 178 |
| Flexural Stress | 250 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 8.0 | -- | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | 55 | -- | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 235 | -- | °C | ISO 75-2/A |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+17 | -- | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 425 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (0.750 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature - Desiccant Dryer | 80.0 | °C | |
| Drying Time - Desiccant Dryer | 2.0 to 20 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 80.0 to 120 | °C |
| Note Message | |
|---|---|
| 1 . | 5 g/l |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tecnoprene® A60K6F NAT005 | SO.F.TER. SPA | PP Homopolymer | Tecnoprene® |
| FERREX® GPP20CS61HB NATURAL | Ferro Corporation | PP, Unspecified | FERREX® |
| Plenco 03509 (Compression) | Plastics Engineering Co. | Phenolic | Plenco |
| POLYCOMPO PE 4020L | POLYCOMPO Co.,Ltd. | LLDPE | POLYCOMPO PE |
| LEXAN™ 263F resin | SABIC Innovative Plastics Europe | PC | LEXAN™ |