"Hifax" HSBM CB 1158 A is a high flow, 10% mineral filled high impact polypropylene copolymer suitable for injection moulding. The grade has been specifically designed for moulding large complex parts that require high impact strength as well as good stiffness. This grade is available in custom colour, pellet form. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.980 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 15 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 1450 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180/1A | ||
| -40°C | 5.0 | kJ/m² | |
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 94.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 46.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 51.0 | °C | ISO 306/B50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom SCR7-7010RF | Spartech Polycom | PC | Spartech |
| Sumitomo DAP FS-10-VO-200-P | Sumitomo Bakelite North America, Inc. | DAP | Sumitomo DAP |
| Unichem 7834 | Colorite Polymers | PVC, Flexible | Unichem |
| PETILEN I 668 (UV) | PETKIM Petrokimya Holding A.S. | HDPE | PETILEN |
| Polifor® TR/30 H-D-R NATURALE | SO.F.TER. SPA | PP Homopolymer | Polifor® |