Iupilon® GSH2010LR Y082
| Category: | PC , Polycarbonate |
| Manufacturer: | Mitsubishi Engineering-Plastics Corp |
| Trademark: | Iupilon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mgibqk_Iupilon-GSH2010LR-Y082.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Iupilon® GSH2010LR Y082 is a Polycarbonate (PC) material filled with 10% glass fiber. It is available in Asia Pacific, Europe, or North America for injection molding. Important attributes of Iupilon® GSH2010LR Y082 are:
Typical application of Iupilon® GSH2010LR Y082: Electrical/Electronic Applications |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.27 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 17 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 15.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Across Flow : 3.20 mm | 0.30 to 0.50 | % | |
| Flow : 3.20 mm | 0.30 to 0.50 | % | |
| Water Absorption (Saturation, 23°C) | 0.14 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3300 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 60.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 4.6 | % | ISO 527-2 |
| Flexural Modulus | 2800 | MPa | ISO 178 |
| Flexural Stress | 105 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 70 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 132 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 131 | °C | ISO 75-2/A |
| CLTE | ISO 11359-2 | ||
| Flow | 5.0E-5 | cm/cm/°C | |
| Transverse | 5.9E-5 | cm/cm/°C |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Comparative Tracking Index (CTI) | PLC 3 | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.400 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 270 to 290 | °C | |
| Middle Temperature | 280 to 300 | °C | |
| Front Temperature | 280 to 300 | °C | |
| Nozzle Temperature | 280 to 300 | °C | |
| Mold Temperature | 80.0 to 120 | °C | |
| Injection Pressure | 50.0 to 150 | MPa | |
| Screw Speed | 50 to 100 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1600 Z L | RTP Company | PAS | RTP |
| RheTech Thermoplastic Polyolefin FT1055-624 | RheTech, Inc. | Polyolefin, Unspecified | RheTech Thermoplastic Polyolefin |
| Ultralloy™ 108 | Hapco Inc. | TP, Unspecified | Ultralloy™ |
| Hostacom TKG 324N Black | LyondellBasell Industries | PP Copolymer | Hostacom |
| LEXAN™ LSHF resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |