| 40% GLASS BEAD FILLED POLYPROPYLENE |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.21 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 1.1 to 1.6 | % | ASTM D955 |
| Water Absorption (Equilibrium) | 0.030 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 22.1 | MPa | ASTM D638 |
| Tensile Elongation (Break) | > 10 | % | ASTM D638 |
| Flexural Modulus | 2210 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 27 | J/m | ASTM D256 |
| Unnotched Izod Impact | 370 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 68.3 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+17 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 76.7 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 227 | °C | |
| Mold Temperature | 37.8 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.013 to 0.025 | mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Starflam MX06089 | Eurostar Engineering Plastics | PP, Unspecified | Starflam |
| BESTDUR TPHG6/01 | Triesa Plastics | PBT+PET | BESTDUR |
| G-Blend 85 HI PC/ABS | Gardiner Compounds Ltd. | PC+ABS | G-Blend |
| InnoPlus HD8100M | PTT Global Chemical Public Company Limited | HDPE | InnoPlus |
| LNP™ LUBRICOMP™ RFL33 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRICOMP™ |