Tislamid® PA6 PA6 30 GBR
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Tisan |
| Trademark: | Tislamid® PA6 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mgf5LX_Tislamid-PA6-PA6-30-GBR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Tislamid® PA6 PA6 30 GBR is a Polyamide 6 (Nylon 6) material filled with 30% glass bead. It is available in Africa & Middle East or Europe for injection molding. Primary attribute of Tislamid® PA6 PA6 30 GBR: Flame Rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.35 | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.90 | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | < 2.0 | % | ISO 62 |
| Ash Content | 30 | % | ISO 3451 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 82 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield | 80.0 | MPa | |
| Break | 79.0 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Yield | 4.3 | % | |
| Break | 4.1 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 5.0 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 200 | °C | ISO 75-2/Be |
| Vicat Softening Temperature | 210 | °C | ISO 306/B120 |
| Melting Temperature | 220 to 225 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (3.00 mm) | 500 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Flammability Index (3.00 mm) | 650 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 100 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 220 to 240 | °C | |
| Middle Temperature | 220 to 240 | °C | |
| Front Temperature | 220 to 240 | °C | |
| Nozzle Temperature | 210 to 230 | °C | |
| Processing (Melt) Temp | 220 to 240 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Clariant Nylon 6/6 PA-113CF30 | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |
| Evoprene™ G 975 | AlphaGary | SEBS | Evoprene™ G |
| Formolene® 5143S | Formosa Plastics Corporation, U.S.A. | PP Homopolymer | Formolene® |
| INEOS PP R35C-01 | INEOS Olefins & Polymers USA | PP Random Copolymer | INEOS PP |
| LUVOCOM® 1105-8971/GY | Lehmann & Voss & Co. | PEEK | LUVOCOM® |