Nypol® PA B3 HS PRTA010 NT388
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Petropol Industry and Trade of Polymers LTDA |
| Trademark: | Nypol® PA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mgGyDX_Nypol-PA-B3-HS-PRTA010-NT388.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Nylon 6 color black, thermic stabilization, good set of mechanical properties, good resistance to traction and elongation, good set of thermal properties. Ideal for injection molding. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.13 to 1.40 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow (3.00 mm) | 1.0 | -- | % | ISO 294-4 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 9.0 | -- | % | |
| Equilibrium, 23°C, 50% RH | 3.0 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 3000 | 1500 | MPa | ISO 527-2 |
| Tensile Strength | ||||
| Yield | 79.0 | 40.0 | MPa | ASTM D638 |
| Yield | 80.0 | 50.0 | MPa | ISO 527-2 |
| -- | 80.0 | 60.0 | MPa | ASTM D638 |
| Tensile Elongation | ||||
| Yield | 4.9 | 23 | % | ASTM D638 |
| Break | 60 | 240 | % | ASTM D638 |
| Break | 50 | 100 | % | ISO 527-2 |
| Flexural Modulus | 2790 | 690 | MPa | ASTM D790 |
| Flexural Strength (5.0% Strain) | 110 | 27.0 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | No Break | No Break | ISO 179/1eU | |
| Notched Izod Impact Strength (23°C) | 5.5 kJ/m² | No Break | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ||||
| 0.45 MPa, Unannealed | 158 | -- | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 160 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 55.0 | -- | °C | ASTM D648, ISO 75-2/A |
| Melting Temperature | 218 | -- | °C | ISO 11357-3 |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Processing (Melt) Temp | 230 to 260 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC M1373 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| RAYPRENE® NB221-S4042 | R&P (Pte.) Ltd. | TPE | RAYPRENE® |
| megol® WR 60 | API SpA | SEBS | megol® |
| TOTAL Polyethylene HDPE 56020 S | TOTAL Refining & Chemicals | HDPE, UHMW | TOTAL Polyethylene |
| Elastocon® 2840PE | Elastocon TPE Technologies | TPE | Elastocon® |