TOTAL Polypropylene PPH 6088
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | TOTAL Refining & Chemicals |
| Trademark: | TOTAL Polypropylene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mfqYAi_TOTAL-Polypropylene-PPH-6088.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polypropylene PPH 6088 is a homopolymer with a Melt Flow Index of 9 g/10 min for the cast extrusion of films with excellent optical properties and good sterilizability. Polypropylene PPH 6088 is formulated with slip and anti-block agents. It is recommended for food packaging, textile packaging, flowers packaging, lamination films and stationary supplies. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.905 | g/cm³ | ISO 1183 |
| Apparent Density | 0.53 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 9.0 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 95 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1400 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 30.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 10 | % | ISO 527-2 |
| Flexural Modulus | 1300 | MPa | ISO 178 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 50 µm, Cast Film | 22.0 | MPa | |
| TD : Yield, 50 µm, Cast Film | 22.0 | MPa | |
| MD : Break, 50 µm, Cast Film | 60.0 | MPa | |
| TD : Break, 50 µm, Cast Film | 55.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 50 µm, Cast Film | 700 | % | |
| TD : Break, 50 µm, Cast Film | 700 | % | |
| Dart Drop Impact (50 µm, Cast Film) | 280 | g | ISO 7765-1 |
| Elmendorf Tear Strength 1 | ISO 6383-2 | ||
| MD : 50.0 µm | 14.0 | kN/m | |
| TD : 50.0 µm | 27.0 | kN/m |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.0 | kJ/m² | ISO 179 |
| Notched Izod Impact Strength (23°C) | 4.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 100 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 55.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 152 | °C | ISO 306/A50 |
| -- | 87.0 | °C | ISO 306/B50 |
| Melting Temperature (DSC) | 160 | °C | ISO 3146 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 50.0 µm, Cast Film) | 89 | ASTM D2457 | |
| Haze (50.0 µm, Cast Film) | 1.4 | % | ISO 14782 |
| Note Message | |
|---|---|
| 1 . | Cast Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SOLLAMID B 2720 | Krisoll Resinas Plásticas Ltda. | Nylon 6 | SOLLAMID |
| Desmoderm® TXC ENB-01 | Covestro - PUR | PUR-Ester | Desmoderm® |
| ExxonMobil™ PP7032KN | ExxonMobil Chemical | PP Impact Copolymer | ExxonMobil™ |
| INEOS PP 101-GF02 | INEOS Olefins & Polymers Europe | PP Homopolymer | INEOS PP |
| Kazan HDPE 271-274K | Kazanorgsintez Joint Stock Company | HDPE | Kazan HDPE |