| Polyamide 6, 15 % glass fiber reinforced, impact modified, natural |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 40.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 23°C, 72 hr | 1.0 | % | |
| Flow : 23°C, 72 hr | 0.70 | % | |
| Ash Content (650°C) | 15 | % | ISO 3451 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5200 | MPa | ISO 527-2/1A/1 |
| Tensile Stress | ISO 527-2/1A/5 | ||
| Yield | 110 | MPa | |
| Break | 110 | MPa | |
| Tensile Strain (Break) | 3.5 | % | ISO 527-2/1A/20 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 16 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 80 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 221 | °C | ISO 11357-3 |
| Note Message | |
|---|---|
| 1 . | 50%RH, between 16 to 72 hrs |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Toyolac® 910-X15 | Toray Resin Company | MABS | Toyolac® |
| Nypol® PA A3 N10 NTLA014 NR329 MSP | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Advanced Composites ADX-5023 | Advanced Composites, Inc. | TPO | Advanced Composites |
| NILAMID® XS3 CF40 | Nilit Plastics | Nylon, Unspecified | NILAMID® |
| Pro-fax 6331 | LyondellBasell Industries | PP Homopolymer | Pro-fax |