ASTAMID™ MB3ZUV
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Marplex Australia Pty. Ltd. |
| Trademark: | ASTAMID™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mdAPym_ASTAMID-MB3ZUV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ASTAMID™ MB3ZUV is an Impact Modified, Heat and UV Stabilised Polyamide 6 (PA 6 or Nylon 6). |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.07 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (235°C/2.16 kg) | 10 | g/10 min | ASTM D1238 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 2.3 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1(3.20 mm) | 1980 | MPa | ASTM D638 |
| Tensile Strength 2(3.20 mm) | 55.0 | MPa | ASTM D638 |
| Tensile Elongation 3(Break, 3.20 mm) | 5.0 | % | ASTM D638 |
| Flexural Modulus 4(3.20 mm) | 1850 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | > 850 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 50.0 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 to 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 250 to 255 | °C | |
| Middle Temperature | 255 to 265 | °C | |
| Front Temperature | 265 to 270 | °C | |
| Processing (Melt) Temp | 255 to 265 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C | |
| Injection Pressure | 60.0 to 120 | MPa | |
| Injection Rate | Fast | ||
| Back Pressure | 0.100 to 0.500 | MPa | |
| Screw Speed | 40 to 60 | rpm | |
| Clamp Tonnage | 3.0 to 5.0 | kN/cm² |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Dynalloy™ OBC 8100-N50 | PolyOne Corporation | TPE | Dynalloy™ |
| Karina WHITE PVC COMPOUND 851-10/1-E-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| POCAN® S 7926 000000 | LANXESS GmbH | PBT | POCAN® |
| CERTENE™ PHT-4 | Muehlstein | PP Homopolymer | CERTENE™ |
| STYRON™ 2678 MED | Trinseo | PS (GPPS) | STYRON™ |