RTP EMI 2863-75A Datasheet,TPO (POE),RTP Company-SHANGHAI SUSHENG

Message
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. Stainless Steel Fiber - Electrically Conductive - EMI/RFI Shielding

General Information
Filler / Reinforcement	Stainless steel fiber, 20% filler by weight
Features	Conductivity Electromagnetic shielding (EMI) Radio frequency shielding (RFI)
RoHS Compliance	Contact manufacturer
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.04	g/cm³	ASTM D792
Molding Shrinkage - Flow (3.20 mm)	1.0 - 1.5	%	ASTM D955
Moisture Content	0.030	%

Electrical	Nominal Value	Unit	Test Method
Static Decay		sec	FTMS 101C 4046.1

Additional Information	Nominal Value	Unit
Primary Additive	20	%

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore A, 10 sec)	76		ASTM D2240

Elastomers	Nominal Value	Unit	Test Method
Tensile Strength (Yield)	2.62	MPa	ASTM D412
Tensile Elongation (Yield)	21	%	ASTM D412
Tear Strength ¹	19.4	kN/m	ASTM D624

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity
-- ²	< 1.0E+4	ohms	ASTM D257
--	< 1.0E+3	ohms	ESD STM11.11
Volume Resistivity	< 10	ohms·cm	ASTM D257

Injection	Nominal Value	Unit
Drying Temperature	79.4	°C
Drying Time	2.0	hr
Dew Point	-17.8	°C
Processing (Melt) Temp	182 - 210	°C
Mold Temperature	15.6 - 65.6	°C
Injection Pressure	82.7 - 124	MPa

Injection instructions
Use a reverse barrel profile. Remove hopper magnets. Allow 4 - 5 shots to properly disperse the conductive fibers. The surface finish should have a silver streaking appearance, not clumps.Use a reverse barrel profile. To maximize fiber length, the following injection barrel, screw, and tip designs should be followed. L/D ratio 16/1 - 22/1, Compression ratio 2:1, Flight depth 0.200 in (5 mm) minimum, in feed section, Screw diameter 0.65 - 0Remove hopper magnets.

Injection instructions

Use a reverse barrel profile. Remove hopper magnets. Allow 4 - 5 shots to properly disperse the conductive fibers. The surface finish should have a silver streaking appearance, not clumps.Use a reverse barrel profile. To maximize fiber length, the following injection barrel, screw, and tip designs should be followed. L/D ratio 16/1 - 22/1, Compression ratio 2:1, Flight depth 0.200 in (5 mm) minimum, in feed section, Screw diameter 0.65 - 0Remove hopper magnets.

Note Message
1 .	C mould
2 .	ESD STM11.11

Category:	TPO (POE) , Thermoplastic Polyolefin Elastomer
Manufacturer:	RTP Company
Trademark:	RTP
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	mcye4S_RTP-EMI-2863-75A.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Purell GC7260	LyondellBasell Industries	HDPE	Purell
TABOND 2003	SILON s.ro	Plastomer	TABOND
Forprene® 6NM919A60	SO.F.TER. SPA	TPV	Forprene®
Garathane™ X 96-322-A NAT	AlphaGary	PVC Alloy	Garathane™
PSM® HL-100B3FH	Wuhan Huali Environmental Technology Co., Ltd.	TP, Unspecified	PSM®