LEXAN™ 144R resin
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LEXAN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mcll8Q_LEXAN144Rresin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Medium viscosity, multi purpose polycarbonate resin with added release agent. Food contact approved in limited colors. Effective January 15th, 2007 this grade will no longer be supported with biocompatibility information and should not be used for medical applications which require biocompatibility. Alternative grade HP3REU. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 12.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow 1 | 0.50 - 0.70 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.35 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.15 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 95.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2350 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 63.0 | MPa | ISO 527-2/50 |
| Fracture | 70.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 6.0 | % | ISO 527-2/50 |
| Fracture | 110 | % | ISO 527-2/50 |
| Flexural Modulus 2 | 2300 | MPa | ISO 178 |
| Flexural Stress | 90.0 | MPa | ISO 178 |
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel) | 10.0 | mg | Internal method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30°C 3 | 14 | kJ/m² | ISO 179/1eA |
| 23°C 4 | 73 | kJ/m² | ISO 179/1eA |
| 23°C | 35 | kJ/m² | ISO 179/2C |
| Charpy Unnotched Impact Strength 5 | ISO 179/1eU | ||
| -30°C | No Break | ISO 179/1eU | |
| 23°C | No Break | ISO 179/1eU | |
| Notched Izod Impact 6 | ISO 180/1A | ||
| -30°C | 12 | kJ/m² | ISO 180/1A |
| 23°C | 70 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | ISO 180/1U | ||
| -30°C 7 | No Break | ISO 180/1U | |
| 23°C 8 | No Break | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 9 | |||
| 0.45 MPa, unannealed, 100 mm span | 136 | °C | ISO 75-2/Be |
| 1.8 MPa, unannealed, 100 mm span | 125 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 153 | °C | ISO 306/A50 |
| -- | 141 | °C | ISO 306/B50 |
| -- | 142 | °C | ISO 306/B120 |
| Ball Pressure Test | IEC 60695-10-2 | ||
| 125°C | Pass | IEC 60695-10-2 | |
| 140°C 10 | Pass | IEC 60695-10-2 | |
| CLTE - Flow (23 to 80°C) | 7.0E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.20 | W/m/K | ISO 8302 |
| RTI Elec | 130 | °C | UL 746 |
| RTI Imp | 125 | °C | UL 746 |
| RTI | 125 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | IEC 60243-1 | ||
| 1.00 mm 11 | 15 | kV/mm | IEC 60243-1 |
| 3.20mm, in oil | 17 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 50 Hz | 2.70 | IEC 60250 | |
| 60 Hz | 2.70 | IEC 60250 | |
| 1 MHz | 2.70 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | ||
| 50 Hz | 1.0E-3 | IEC 60250 | |
| 60 Hz | 1.0E-3 | IEC 60250 | |
| 1 MHz | 0.010 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | HB | UL 94 | |
| 3.00 mm | HB | UL 94 | |
| Glow Wire Flammability Index (1.00 mm) | 850 | °C | IEC 60695-2-12 |
| Oxygen Index | 25 | % | ISO 4589-2 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.586 | ISO 489 | |
| Transmittance (2540 µm) | 88.0 - 90.0 | % | ASTM D1003 |
| Haze (2540 µm) | < 0.80 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 60.0 - 80.0 | °C | |
| Rear Temperature | 260 - 280 | °C | |
| Middle Temperature | 270 - 290 | °C | |
| Front Temperature | 280 - 310 | °C | |
| Nozzle Temperature | 270 - 290 | °C | |
| Processing (Melt) Temp | 280 - 310 | °C | |
| Mold Temperature | 80.0 - 110 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*3 sp=62mm |
| 4 . | 80*10*3 sp=62mm |
| 5 . | 80*10*3 sp=62mm |
| 6 . | 80*10*3 |
| 7 . | 80*10*3 |
| 8 . | 80*10*4 |
| 9 . | 120*10*4 mm |
| 10 . | Approximate maximum |
| 11 . | Short-Time |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Next ABS SXT4-02ABK | Next Polymers Ltd. | ABS | Next ABS |
| Adell PP ER-39 | Adell Plastics, Inc. | PP Homopolymer | Adell PP |
| ADENE GCJB | A.D. Compound spa | PP Homopolymer | ADENE |
| Evermore PUR B-6312N | Evermore Chemical Industry Co., Ltd. | PUR, Unspecified | Evermore PUR |
| OTECH PVC PL1001-11 - Plenum Insulation | OTECH Corporation | PVC, Unspecified | OTECH PVC |