TAFMER™ A-1070S
| Category: | PAO , Polyalphaolefin |
| Manufacturer: | Mitsui Chemicals America, Inc. |
| Trademark: | TAFMER™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mclEdk_TAFMER-A-1070S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TAFMER™ A-1070S is a Polyalphaolefin (PAO) material. It is available in North America. Primary attribute of TAFMER™ A-1070S: Good Flexibility. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.870 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/2.16 kg | 1.2 | g/10 min | |
| 230°C/2.16 kg | 2.2 | g/10 min | |
| Mooney Viscosity (ML 1+4) | 40 | MU | JIS K6395 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 73 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | > 14.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | > 1000 | % | ASTM D638 |
| Torsional Rigidity | 3.00 | MPa | ASTM D1043 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -70.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 41.0 | °C | ASTM D1525 |
| Melting Temperature | 55.0 | °C | ASTM D2117 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+17 | ohms·cm | ASTM D257 |
| Dielectric Constant | 2.20 to 2.40 | ASTM D150 | |
| Dissipation Factor | < 5.0E-4 | ASTM D150 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 280.8 | RTP Company | Nylon 66 | RTP |
| SILVER® ABS 3360E | Guangdong Silver Age Sci & Tech. Co., Ltd | ABS | SILVER® |
| ACRYREX® CM-205G | CHI MEI CORPORATION | Acrylic (PMMA) | ACRYREX® |
| Baydur® GS-772 | Covestro - PUR | PUR-MDI | Baydur® |
| HOPELEN SFR-171H | Lotte Chemical Corporation | PP Homopolymer | HOPELEN |