LNP™ THERMOCOMP™ QF0069 compound
| Category: | Nylon 610 , Polyamide 610 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mcNWbR_LNP-THERMOCOMP-QF0069-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP QF0069 is a compound based on Nylon 6/10 resin containing 30% Glass Fiber. Added features of this material include: Flame Retardant. Also known as: LNP* THERMOCOMP* Compound QF-1006 FR-1 Product reorder name: QF0069 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.56 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.20 to 0.40 | % | ASTM D955 |
| Across Flow : 24 hr | 0.80 to 1.0 | % | ASTM D955 |
| Across Flow : 24 hr | 0.86 | % | ISO 294-4 |
| Flow : 24 hr | 0.29 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.10 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 11000 | MPa | ASTM D638 |
| -- | 11000 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 150 | MPa | ASTM D638 |
| Yield | 145 | MPa | ISO 527-2 |
| Break | 150 | MPa | ASTM D638 |
| Break | 145 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 2.0 | % | ASTM D638 |
| Yield | 1.8 | % | ISO 527-2 |
| Break | 2.0 | % | ASTM D638 |
| Break | 1.8 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 9650 | MPa | ASTM D790 |
| -- | 9000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 200 | MPa | ASTM D790 |
| -- | 197 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 64 | J/m | ASTM D256 |
| 23°C 2 | 6.4 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 600 | J/m | ASTM D4812 |
| 23°C 3 | 37 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 9.50 | J | ASTM D3763 |
| -- | 2.10 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 220 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 4 | 218 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 201 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 5 | 197 | °C | ISO 75-2/Af |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 6.7E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 4.0E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.12 to 0.20 | % | |
| Rear Temperature | 249 to 260 | °C | |
| Middle Temperature | 260 to 271 | °C | |
| Front Temperature | 271 to 282 | °C | |
| Processing (Melt) Temp | 271 to 277 | °C | |
| Mold Temperature | 82.2 to 93.3 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polypropylene Lumicene® M 3661 | TOTAL Refining & Chemicals | PP Homopolymer | TOTAL Polypropylene |
| UBE Polyethylene L719 | UBE America, Inc. | PE, Unspecified | UBE Polyethylene |
| Adell Polyamide BR-37 | Adell Plastics, Inc. | Nylon 6 | Adell Polyamide |
| Geon™ Vinyl Flexible A5DU0 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| GLS ABS SN08 | GLS Polymers Pvt. Ltd. | ABS | GLS ABS |