AKROMID® B3 GF 30 1 XL black (4366)
| Category: | Nylon 6+PP , Polyamide 6 + PP |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mbQXC3_AKROMID-B3-GF-30-1-XL-black-4366-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROMID® B3 GF 30 1 XL black (4366) is a 30% glass fibre reinforced and heat stabilised polyamide-blend with a greatly reduced density compared to standard PA6 GF 30 Applications are mainly technical components in the automotive and electronic industry, where a weight and cost reduction is required |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.22 | -- | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 9.00 | -- | cm³/10min | ISO 1133 |
| Spiral Flow | 78.5 | -- | cm | Internal Method |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.90 | -- | % | |
| Flow | 0.40 | -- | % | |
| Humidity Absorption - 62% RH (70°C) | 1.0 | -- | % | ISO 1110 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flexural Strain at Break 1 | 3.2 | -- | % | ISO 178 |
| Additional Information | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Reinforcement Content | 30 | -- | % | ISO 1172 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 150 | -- | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 8200 | 6800 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 115 | 100 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 3.0 | 3.5 | % | ISO 527-2/5 |
| Flexural Modulus 2 | 8700 | -- | MPa | ISO 178 |
| Flexural Stress 3 | 184 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 13 | 13 | kJ/m² | |
| 23°C | 12 | 13 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 45 | 42 | kJ/m² | |
| 23°C | 48 | 48 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 186 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 160 | -- | °C | ISO 75-2/A |
| Melting Temperature 4 | 220 | -- | °C | DIN EN 11357-1 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Comparative Tracking Index (Solution A) | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate 5(1.00 mm) | < 100 | -- | mm/min | FMVSS 302 |
| Flame Rating (0.800 mm) | HB | -- | UL 94 | |
| Glow Wire Flammability Index (0.800 mm) | 650 | -- | °C | IEC 60695-2-12 |
| Note Message | |
|---|---|
| 1 . | 2 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 10 K/min, DSC |
| 5 . | >1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 200 MS 5 | RTP Company | Nylon 66 | RTP |
| RTP ESD C 2700-50A | RTP Company | SEBS | RTP |
| SEMICOSIL® 911 A/B | Wacker Chemie AG | Silicone | SEMICOSIL® |
| Chansieh Phenolic J-185 | Chansieh Enterprises Co., LTD. | Phenolic | Chansieh Phenolic |
| Fusabond® C190 | DuPont Packaging & Industrial Polymers | EVA | Fusabond® |