| VA-1810 is a 80 shore A polyurethane elastomer formulated for hand-batch processing, vacuum assisted processing or meter mix dispensed. Excellent physical properties can be obtained with a room temperature cure without the utilization of mercury. MOCA, or TDI. VA-1810 has excellent green strength for quick demold times. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| Cured | 1.12 | g/cm³ | |
| Hardener | 1.14 | g/cm³ | |
| Base Resin | 1.21 | g/cm³ | |
| Molding Shrinkage - Flow | 0.20 to 0.50 | % | ASTM D2566 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Volume: 100 Mix Ratio by Weight: 100 | ||
| Resin | Mix Ratio by Weight: 80 Mix Ratio by Volume: 72 | ||
| Demold Time | 60 to 120 | min |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Viscosity | |||
| 25°C 1 | 0.55 | Pa·s | |
| 25°C 2 | 1.8 | Pa·s | |
| 25°C 3 | 4.5 | Pa·s | |
| Curing Time 4 | 25 | hr | |
| Gel Time | 8.0 to 12 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore A) | 70 to 80 | ASTM D2240 | |
| Tensile Strength | 6.21 | MPa | ASTM D638 |
| Tensile Elongation at Break | 100 | % | ASTM D638 |
| Tear Strength | 14.0 | kN/m | ASTM D624 |
| Note Message | |
|---|---|
| 1 . | Hardener |
| 2 . | Mixed |
| 3 . | Resin |
| 4 . | 24 hours at 77°F + 1 hour at 150°F |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VITAMIDE® BW36 | A. Schulman Europe | Nylon 6 | VITAMIDE® |
| Unipren® Elastomers B3 NTLA010 75A UP311 | Petropol Industry and Trade of Polymers LTDA | PP+EPDM | Unipren® Elastomers |
| Hapflex™ 780 | Hapco Inc. | TP, Unspecified | Hapflex™ |
| Karina CLEAR PVC COMPOUND 65/213 | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LEXAN™ 144R resin | SABIC Innovative Plastics | PC | LEXAN™ |