SABIC® PP 58MNK10
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mb2gKS_SABIC-PP-58MNK10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This grade combines an excellent stiffness with high impact resistance. It has a narrow molecular weight distribution and a low tendency to warp. Excellent flow in combination with high crystallisation speed enables outstanding processability aiming at easy mould filling and short cycle times. Due to the mentioned performance this grade is suitable for usage in several kinds of containers. The excellent high gloss level makes this material also favourable for household applications. This product is not intended for and must not be used in any pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.905 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 15 | g/10 min | ASTM D1238, ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 97 | ASTM D785 | |
| Shore Hardness (Shore D) | 65 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 1% Secant 1 | 1600 | MPa | ASTM D638 |
| -- | 1550 | MPa | ISO 527-2/1A/1 |
| Tensile Strength | |||
| Yield 2 | 26.0 | MPa | ASTM D638 |
| Yield | 27.0 | MPa | ISO 527-2/1A/50 |
| Tensile Elongation | |||
| Yield 3 | 4.0 | % | ASTM D638 |
| Yield | 4.0 | % | ISO 527-2/1A/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 6.0 | kJ/m² | |
| 0°C | 8.0 | kJ/m² | |
| 23°C | 13 | kJ/m² | |
| Notched Izod Impact | |||
| -20°C | 65 | J/m | ASTM D256A |
| 0°C | 75 | J/m | ASTM D256A |
| 23°C | 100 | J/m | ASTM D256A |
| -20°C | 6.0 | kJ/m² | ISO 180/1A |
| 0°C | 7.0 | kJ/m² | ISO 180/1A |
| 23°C | 11 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 105 | °C | ASTM D648 |
| 0.45 MPa, Unannealed 4 | 100 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 65.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed 5 | 60.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 151 | °C | ASTM D1525, ISO 306/A120 6 6 |
| -- | 80.0 | °C | ASTM D1525, ISO 306/B120 7 7 |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | testbar 80*10*4mm |
| 5 . | testbar 80*10*4mm |
| 6 . | Rate B (120°C/h), Loading 1 (10 N) |
| 7 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNO ABS 130 | Techno Polymer Co, Ltd. | ABS | TECHNO ABS |
| Nypol® PA A3 G30 P20 PRTA010 NR428 MSP | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Gallonprene® GP540-7504(n)F | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| HiFill® PA6 GF33 HS L | Techmer Engineered Solutions | Nylon 6 | HiFill® |
| Pier One POM AC127-NAT | Pier One Polymers, Inc. | Acetal (POM) Copolymer | Pier One POM |