Lutene® H BE0350
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lutene® H |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mZTm9V_Lutene-H-BE0350.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LUTENE-H BE0350 is an excellent material for blow-molded articles with high density and rigidity. It has good flow characteristics, high parison stability and impact resistance. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.958 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/2.16 kg | 0.25 | g/10 min | ASTM D1238 |
| 190°C/21.6 kg | 20 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (F50) | 40.0 | hr | ASTM D1693 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 64 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 2.94 | MPa | ASTM D638 |
| Tensile Elongation (Break) | > 500 | % | ASTM D638 |
| Flexural Modulus | 1200 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 440 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 76.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 130 | °C | ASTM D1525 1 |
| Melting Temperature 2 | 134 | °C | DSC |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Adapter Temperature | 175 - 190 | °C | |
| Melt Temperature (Aim) | 180 | °C | |
| Die Temperature | 160 - 190 | °C |
| Extrusion instructions |
|---|
| Feeding Zone: 160 - 185 °CCompression Zone: 175 - 195 °CMetering Zone: 180 - 200 °CHead Temperature: 165 - 195°C |
| Note Message | |
|---|---|
| 1 . | 速率 A (50°C/h) |
| 2 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VECTRA® S540 | Celanese Corporation | LCP | VECTRA® |
| Witcom PBT 6G/2L3 | Witcom Engineering Plastics B.V. | PBT | Witcom PBT |
| KumhoSunny PC/ABS HAC8250NH | Shanghai KumhoSunny Plastics Co., Ltd. | PC+ABS | KumhoSunny PC/ABS |
| LNP™ LUBRICOMP™ DZL24 compound | SABIC Innovative Plastics | PC | LNP™ LUBRICOMP™ |
| Kinta NB6030G | Kinta Technology (Hong Kong) Co., Ltd. | Nylon 6 | Kinta |