LEXAN™ 505R resin
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LEXAN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mZLG3q_LEXAN505Rresin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LEXAN 505R Polycarbonate (PC) resin is a 10% glass fiber filled, injection moldable grade. LEXAN 505R contains non-chlorinated, non-brominated flame retardant systems with UL-94 V0 rating at 1.5mm. It is available in various opaque color options for high stiffness applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.26 | g/cm³ | ASTM D792 |
| -- | 1.25 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 7.0 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 7.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow | Internal method | ||
| -- 1 | 0.20 - 0.60 | % | Internal method |
| 3.20 mm | 0.50 - 0.70 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.31 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.13 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 115 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 2 | 3930 | MPa | ASTM D638 |
| -- | 3300 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 3 | 63.0 | MPa | ASTM D638 |
| Yield | 60.0 | MPa | ISO 527-2/5 |
| Fracture 4 | 48.0 | MPa | ASTM D638 |
| Fracture | 45.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 5 | 3.0 | % | ASTM D638 |
| Yield | 5.0 | % | ISO 527-2/5 |
| Fracture 6 | 12 | % | ASTM D638 |
| Fracture | 7.0 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0mm span 7 | 3530 | MPa | ASTM D790 |
| -- 8 | 3400 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 95.0 | MPa | ISO 178 |
| Fracture, 50.0mm span 9 | 108 | MPa | ASTM D790 |
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel) | 11.0 | mg | Internal method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30°C 10 | 9.0 | kJ/m² | ISO 179/1eA |
| 23°C 11 | 9.0 | kJ/m² | ISO 179/1eA |
| 23°C 12 | 10 | kJ/m² | ISO 179/1eA |
| 23°C | 15 | kJ/m² | ISO 179/2C |
| Charpy Unnotched Impact Strength 13 | ISO 179/1eU | ||
| -30°C | No Break | ISO 179/1eU | |
| 23°C | No Break | ISO 179/1eU | |
| Notched Izod Impact | |||
| -30°C | 80 | J/m | ASTM D256 |
| 23°C | 110 | J/m | ASTM D256 |
| -30°C 14 | 8.0 | kJ/m² | ISO 180/1A |
| 23°C 15 | 10 | kJ/m² | ISO 180/1A |
| 23°C 16 | 8.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1600 | J/m | ASTM D4812 |
| -30°C 17 | No Break | ISO 180/1U | |
| -30°C 18 | 130 | kJ/m² | ISO 180/1U |
| 23°C 19 | No Break | ISO 180/1U | |
| Instrumented Dart Impact (23°C, Total Energy) | 61.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 143 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 100 mm span 20 | 144 | °C | ISO 75-2/Be |
| 1.8 MPa, unannealed, 3.20mm | 138 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 100 mm span 21 | 136 | °C | ISO 75-2/Ae |
| 1.8 MPa, annealed 22 | 136 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 149 | °C | ASTM D1525 23 |
| -- | 141 | °C | ISO 306/B50 |
| -- | 143 | °C | ISO 306/B120 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 4.7E-5 | cm/cm/°C | ASTM E831 |
| Flow : 23 to 80°C | 4.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 8.5E-5 | cm/cm/°C | ASTM E831 |
| Lateral : 23 to 80°C | 7.0E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.21 | W/m/K | ISO 8302 |
| RTI Elec | 130 | °C | UL 746 |
| RTI Imp | 130 | °C | UL 746 |
| RTI | 130 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | IEC 60243-1 | ||
| 0.800mm, in oil | 33 | kV/mm | IEC 60243-1 |
| 1.60mm, in oil | 25 | kV/mm | IEC 60243-1 |
| 3.20mm, in oil | 16 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 50 Hz | 2.90 | IEC 60250 | |
| 60 Hz | 2.90 | IEC 60250 | |
| 1 MHz | 2.80 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | ||
| 50 Hz | 1.0E-3 | IEC 60250 | |
| 60 Hz | 1.0E-3 | IEC 60250 | |
| 1 MHz | 0.010 | IEC 60250 | |
| Comparative Tracking Index | 150 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-0 | UL 94 | |
| 2.00 mm, Testing by SABIC | 5VB | UL 94 | |
| 3.00 mm | 5VA | UL 94 | |
| Glow Wire Flammability Index (1.00 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (1.00 mm) | 825 | °C | IEC 60695-2-13 |
| Oxygen Index | 37 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 60.0 - 80.0 | °C | |
| Rear Temperature | 270 - 300 | °C | |
| Middle Temperature | 280 - 310 | °C | |
| Front Temperature | 290 - 320 | °C | |
| Nozzle Temperature | 280 - 310 | °C | |
| Processing (Melt) Temp | 290 - 320 | °C | |
| Mold Temperature | 80.0 - 120 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | Type 1, 5.0 mm/min |
| 5 . | Type 1, 5.0 mm/min |
| 6 . | Type 1, 5.0 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | 1.3 mm/min |
| 10 . | 80*10*3 sp=62mm |
| 11 . | 80*10*4 sp=62mm |
| 12 . | 80*10*3 sp=62mm |
| 13 . | 80*10*4 sp=62mm |
| 14 . | 80*10*4 |
| 15 . | 80*10*3 |
| 16 . | 80*10*4 |
| 17 . | 80*10*4 |
| 18 . | 80*10*3 |
| 19 . | 80*10*3 |
| 20 . | 120*10*4 mm |
| 21 . | 120*10*4 mm |
| 22 . | 2 hr, 120°C |
| 23 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1301 P-1 | RTP Company | PPS | RTP |
| Moplen EP548T | LyondellBasell Industries | PP Impact Copolymer | Moplen |
| NEFTEKHIM PP 1425J (T28C) | Nizhnekamskneftekhim Inc. | PP Homopolymer | NEFTEKHIM PP |
| Axiall PVC 13872 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Durethan® AKV 30 XTS1 901510 | LANXESS GmbH | Nylon 66 | Durethan® |