VECTRA® E130G
| Category: | LCP , Liquid Crystal Polymer |
| Manufacturer: | Celanese Corporation |
| Trademark: | VECTRA® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mYmA8F_VECTRA-E130G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
30% glass fiber filled / low injection pressure Chemical abbreviation according to ISO 1043-1 : LCP Inherently flame retardant UL-Listing V-0 in natural and black at 0.75mm thickness per UL 94 flame testing. Relative-Temperature-Index (RTI) according to UL 746B: electricals 130°C, mechanicals 130°C. UL = Underwriters Laboratories (USA) |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.61 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 12000 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 140 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2/1A/5 |
| Flexural Modulus (23°C) | 12000 | MPa | ISO 178 |
| Flexural Stress (23°C) | 170 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 25 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 273 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 245 | °C | ISO 75-2/A |
| Melting Temperature 1 | 335 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 5.0E-6 | cm/cm/°C | ISO 11359-2 |
| Lateral | 6.7E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.750 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 - 170 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.010 | % | |
| Rear Temperature | 315 - 335 | °C | |
| Middle Temperature | 320 - 345 | °C | |
| Front Temperature | 325 - 355 | °C | |
| Nozzle Temperature | 335 - 350 | °C | |
| Processing (Melt) Temp | 335 - 355 | °C | |
| Mold Temperature | 80.0 - 120 | °C | |
| Injection Pressure | 50.0 - 150 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 50.0 - 150 | MPa |
| Injection instructions |
|---|
| Zone 4 Temperature: 330 to 360°C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| tefabloc® TP SD 310 80A | Mitsubishi Chemical Performance Polymers, Inc. | TPE | tefabloc® |
| TRIBOCOMP® PPS GF30 TS0 | EPIC Polymers | PPS | TRIBOCOMP® |
| DENKA ABS QF | Denka Company Limited | ABS | DENKA ABS |
| Flontech® FT-GL5-M5-1 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| Exceed™ XP 8358ML | ExxonMobil Chemical | PP Elastomer | Exceed™ XP |