EXCELLEN® GMH GH030
| Category: | PE, Unspecified , Polyethylene |
| Manufacturer: | Sumitomo Chemical Asia |
| Trademark: | EXCELLEN® GMH |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mYSR0I_EXCELLEN-GMH-GH030.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Applications For sealant film, greenhouse film, sheet, shoe sole, tube, pipe, etc. Characteristics High mechanical strength, impact resistance, easy processing, seal strength, high speed processing. GH030 is additives free. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.912 | g/cm³ | JIS K7112 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.50 | g/10 min | JIS K6922-1 |
| Environmental Stress-Cracking Resistance | > 1000 | hr | JIS K6760-1981 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 49 | JIS K7215 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 30.0 | MPa | JIS K7113 |
| Tensile Elongation (Break) | 850 | % | JIS K7113 |
| Flexural Modulus | 130 | MPa | ASTM D747-70 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| secant modulus | Internal method | ||
| 1% secant, MD | 110 | MPa | Internal method |
| 1% secant, TD | 130 | MPa | Internal method |
| Tensile Strength | JIS K6781 | ||
| MD : Fracture | 32.0 | MPa | JIS K6781 |
| TD : Fracture | 34.0 | MPa | JIS K6781 |
| Tensile Elongation | JIS K6781 | ||
| MD : Fracture | 550 | % | JIS K6781 |
| TD : Fracture | 710 | % | JIS K6781 |
| Dart Drop Impact | 74 | g | ASTM D1709A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Impact Strength | 1160 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 90.0 | °C | JIS K7206 1 |
| Melting Temperature | 102 | °C | DSC |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°) | 115 | JIS K7105 | |
| Haze | 4.0 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Die Temperature | 150 - 170 | °C |
| Extrusion instructions |
|---|
| Die Gap: Recommended <1.5mmBlow-up Ratio: 2 to 3 (Recommended >2.5) |
| Note Message | |
|---|---|
| 1 . | 压 力1 (10N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 285 H | RTP Company | Nylon 66 | RTP |
| WPP PP PPH5TF2-Black | Washington Penn Plastic Co. Inc. | PP Homopolymer | WPP PP |
| INSTRUC FEPGF10 | Infinity LTL Engineered Compounds | FEP | INSTRUC |
| Paxon™ EA55-003 | ExxonMobil Chemical | HDPE, UHMW | Paxon™ |
| Hostacom EP3307 G12771 | LyondellBasell Industries | PP Copolymer | Hostacom |