Miramid® S3C
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | BASF Leuna GmbH |
| Trademark: | Miramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mYMvGq_Miramid-S3C.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Miramid® S3C is a Polyamide 66 (Nylon 66) material. It is available in Europe for injection molding. Important attributes of Miramid® S3C are:
Typical applications include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1130 | -- | kg/m³ | ISO 1183 1 |
| Water Absorption | ISO 62 2 | |||
| Saturation | 8.0 | -- | % | |
| Equilibrium | 2.5 | -- | % | |
| Viscosity number | 145 | -- | cm³/g | ISO 307, 1157, 1628 3 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile modulus | 3000 | 1800 | MPa | ISO 527-2 4 |
| Tensile Stress (Yield) | 80.0 | 60.0 | MPa | ISO 527-2 5 |
| Tensile Strain (Yield) | 5.0 | 20 | % | ISO 527-2 6 |
| Nominal Tensile Strain at Break | 20 | > 50 | % | ISO 527-2/50 |
| Flexural Modulus | 2500 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy notched impact strength | ISO 179/1eA 7 | |||
| -30°C | 3.00 | -- | kJ/m² | |
| 23°C | 5.00 | 25.0 | kJ/m² | |
| Charpy impact strength | ISO 179/1eU 8 | |||
| -30°C | No Break | -- | ||
| 23°C | No Break | No Break |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ISO 75-2 9 | |||
| 0.45 MPa | 200 | -- | °C | |
| 1.8 MPa | 70.0 | -- | °C | |
| Melting Temperature (DSC) | 260 | -- | °C | ISO 3146 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume resistivity | 1.0E+13 | 1.0E+10 | ohms·m | IEC 60093 10 |
| Dielectric Constant (1 MHz) | 3.40 | 5.00 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.025 | 0.20 | IEC 60250 11 | |
| Comparative tracking index | 600 | -- | IEC 60112 12 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 70.0 to 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 2 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 3 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 4 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 5 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 6 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 7 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 8 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 9 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 10 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 11 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 12 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC V861 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| RTP 1005 HI | RTP Company | PBT | RTP |
| Hostacom TSOP EM5 2657 | LyondellBasell Industries | PP Copolymer | Hostacom |
| LNP™ KONDUIT™ OX10324 compound | SABIC Innovative Plastics Asia Pacific | PPS | LNP™ KONDUIT™ |
| Paracril® 33.80XL | INSA | NBR | Paracril® |