Quadrant EPP TIVAR® DrySlide
| Category: | UHMWPE , Ultra High Molecular Weight Polyethylene |
| Manufacturer: | Quadrant Engineering Plastic Products |
| Trademark: | Quadrant EPP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mXyEmR_Quadrant-EPP-TIVAR-DrySlide.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TIVAR DrySlide is a modified grade of UHMW polymer that has been custom blended to provide a reduced coefficient of friction and enhanced surface lubricity. This reduction in surface coefficient of friction enables TIVAR DrySlide to offer unique advantages for applications in the parcel handling industry where maximum surface lubricity is required. TIVAR DrySlide is static reduced and UV stabilized. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.940 | g/cm³ | ASTM D792 |
| Water Absorption | ASTM D570 | ||
| 24 hr | < 0.010 | % | |
| Saturation | < 0.010 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 64 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 800 | MPa | ASTM D638 |
| Tensile Strength (Ultimate) | 33.1 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 200 | % | ASTM D638 |
| Flexural Modulus | 731 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 21.4 | MPa | ASTM D790 |
| Compressive Modulus | 552 | MPa | ASTM D695 |
| Compressive Strength (10% Strain, 23°C) | 20.0 | MPa | ASTM D695 |
| Coefficient of Friction (vs. Steel - Static) | 0.080 | Internal Method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | No Break | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 46.7 | °C | ASTM D648 |
| Maximum Use Temperature - Long Term, Air | 82 | °C |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Limiting Pressure Velocity 1 | 0.0701 | MPa·m/s | Internal Method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Crystallization Temperature (DSC) | 135 | °C | ASTM D3418 |
| CLTE - Flow 2(-40 to 149°C) | 3.4E-4 | cm/cm/°C | ASTM E831 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+5 to 1.0E+9 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.18 mm, Estimated Rating) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 4:1 safety factor |
| 2 . | 68°F |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYPRO® 5014L ASL015 | YUHWA Korea Petrochemical Ind. Co., Ltd. | PP Homopolymer | POLYPRO® |
| SABIC® LLDPE 726Q | Saudi Basic Industries Corporation (SABIC) | LLDPE | SABIC® LLDPE |
| NITRIFLEX N-300 | NITRIFLEX | NBR | NITRIFLEX |
| GAPEX® FPP30GQ18HB TAN | Ferro Corporation | PP, Unspecified | GAPEX® |
| K-Prene GLC 6070 | Technovinyl Polymers India Ltd. | TPE | K-Prene |