POLYfill PPH B8065 VT1
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Polykemi AB |
| Trademark: | POLYfill |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mXf0XR_POLYfill-PPH-B8065-VT1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Mineral reinforced Heat resistant |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.86 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 8.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 1.1 to 1.4 | % | |
| Flow | 1.1 to 1.4 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 18.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 5.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 3200 | MPa | ISO 178 |
| Flexural Stress | 35.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 2.0 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 1 | |||
| 0.45 MPa, Unannealed | 145 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 70.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 150 | °C | ISO 306/A50 |
| -- | 100 | °C | ISO 306/B50 |
| Note Message | |
|---|---|
| 1 . | 120°C/hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| AMPLIFY™ IO 3802 | The Dow Chemical Company | Ionomer | AMPLIFY™ IO |
| Daelim Po1y® PP-180 | DAELIM INDUSTRIAL CO., LTD. | PP Homopolymer | Daelim Po1y® |
| HOPELEN FC-150B | Lotte Chemical Corporation | PP Homopolymer | HOPELEN |
| LIHAN® I706 | Nanjing Lihan Chemical Co., Ltd. | PEI | LIHAN® |
| LNP™ STAT-KON™ DX12411C compound | SABIC Innovative Plastics | PC | LNP™ STAT-KON™ |