Wellamid® GF14-60 XE-N
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Wellman Engineering Resins |
| Trademark: | Wellamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mXec2r_Wellamid-GF14-60-XE-N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Wellamid® GF14-60 XE-N is a Polyamide 6 (Nylon 6) material filled with 14% glass fiber. It is available in Asia Pacific, Europe, Latin America, or North America for injection molding. Typical application of Wellamid® GF14-60 XE-N: Automotive |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.22 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow : 23°C | 0.70 to 1.1 | % | |
| Flow : 23°C | 0.40 to 0.80 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield, 23°C) | 125 | MPa | ISO 527-2 |
| Tensile Strain (Yield, 23°C) | 4.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 4900 | MPa | ISO 178 |
| Flexural Stress (23°C) | 175 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 5.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 200 | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 220 | °C | ISO 3146 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 260 to 282 | °C | |
| Middle Temperature | 254 to 277 | °C | |
| Front Temperature | 249 to 271 | °C | |
| Nozzle Temperature | 249 to 271 | °C | |
| Processing (Melt) Temp | 254 to 282 | °C | |
| Mold Temperature | 71.1 to 93.3 | °C | |
| Injection Pressure | 34.5 to 138 | MPa | |
| Back Pressure | 0.345 | MPa | |
| Screw Speed | 30 to 120 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1028 | RTP Company | PBT | RTP |
| TAROBLEND 85 X0 | Taro Plast S.p.A. | PC+ABS | TAROBLEND |
| Generic Nylon 66 - Glass Fabric | Generic | Nylon 66 | Generic |
| Karina IVORY PVC COMPOUND 75920-35/1-B-AC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Petrothene® XL07407 | LyondellBasell Industries | Polyolefin, Unspecified | Petrothene® |