Cellophane™ 400PUT
| Category: | Cellulose, Regenerated , Regenerated Cellulose |
| Manufacturer: | Innovia Films Ltd. |
| Trademark: | Cellophane™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mXSGlb_Cellophane-400PUT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Non Heat-Sealable Tape Base Films Uncoated regenerated cellulose film (RCF) with high mechanical strength. 400/450/500PUT have been developed for use as a base for the manufacture of adhesive tapes. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | ASTM D1894 | ||
| vs. Itself - Dynamic | 0.50 | ||
| vs. Itself - Static | 0.70 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 28 | µm | |
| Secant Modulus | ASTM D882 | ||
| 1% Secant, MD : 28 µm | > 3000 | MPa | |
| 1% Secant, TD : 28 µm | > 1500 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 28 µm | 125 | MPa | |
| TD : Yield, 28 µm | 70.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 28 µm | 22 | % | |
| TD : Break, 28 µm | 70 | % | |
| Oxygen Transmission Rate (Wet) (23°C, 28 µm, 0.0% RH) | 1.00 | cm³/m²/24 hr | ASTM F1927 |
| Yield (27.7 µm) | 25.0 | m²/kg | Internal Method |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rilsan® BESN Noir TL | Arkema | Nylon 11 | Rilsan® |
| Sumitomo Phenolic FM 4005X4648 | Sumitomo Bakelite North America, Inc. | Phenolic | Sumitomo Phenolic |
| LAMINEX® 2140 | Schwartz Technical Plastic | PF | LAMINEX® |
| LNP™ THERMOCOMP™ MC004 compound | SABIC Innovative Plastics Europe | PP, Unspecified | LNP™ THERMOCOMP™ |
| LUVOCOM® 1100-8721/EM/BK | Lehmann & Voss & Co. | PESU | LUVOCOM® |