Huafon T27
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Huafon Group Co., Ltd. |
| Trademark: | Huafon |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mWlOyN_Huafon-T27.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
T27 is light medium viscosity resin. Typical Applications T27 is broadly used in product of nylon 66 monofilament, staple, carpet yarn. as well as in compounding plastics. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (275°C/2.16 kg) | 66 | g/10 min | ISO 1133 |
| Particle Size | 1.40 to 2.00 | g/100 pellets | Internal Method |
| Relative Viscosity | Internal Method | ||
| Dry Chips | 2.66 to 2.74 | ||
| Wet Chips | 2.61 to 2.69 | ||
| Water Content | Internal Method | ||
| Dry Chips | < 800 | mg/kg | |
| Wet Chips | < 5000 | mg/kg |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1 | 75.8 | MPa | ISO 527-2 |
| Tensile Strain 2(Break) | 66 | % | ISO 527-2 |
| Flexural Modulus 3 | 2640 | MPa | ISO 178 |
| Flexural Stress 4 | 99.9 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 5(23°C) | 6.2 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 6 | |||
| 0.45 MPa, Annealed | 185 | °C | ISO 75-2/B |
| 1.8 MPa, Annealed | 68.4 | °C | ISO 75-2/A |
| Vicat Softening Temperature 7 | 240 | °C | ISO 306/B120 |
| Peak Melting Temperature 8 | 267 | °C | ASTM D3418 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating 9 | UL 94 | ||
| 1.00 mm | V-2 | ||
| 1.60 mm | V-2 | ||
| 3.00 mm | V-2 |
| Note Message | |
|---|---|
| 1 . | 48h/23°C/50%RH |
| 2 . | 48h/23°C/50%RH |
| 3 . | 48h/23°C/50%RH |
| 4 . | 48h/23°C/50%RH |
| 5 . | 48h/23°C/50%RH |
| 6 . | 48h/23°C/50%RH |
| 7 . | 48h/23°C/50%RH |
| 8 . | 10°C/min |
| 9 . | 48h/23°C/50%RH |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 205B TFE 15 FR | RTP Company | Nylon 610 | RTP |
| T-Blend® 5292N-PE | TSRC Corporation | TPE | T-Blend® |
| Multi-Flex® TPE TES 2403 SI1 BLK - PL23095 | Multibase, A Dow Corning Company | TES | Multi-Flex® TPE |
| Durethan® BKV 30 G H2.0 900051 | LANXESS Corporation | Nylon 6 | Durethan® |
| FRAGOM PR/112 UTW | Crosspolimeri S.p.A. | Polyolefin, Unspecified | FRAGOM |