UmaPET WHHSO Datasheet,PET,Ester Industries Ltd.-SHANGHAI SUSHENG

Message
KEY FEATURES Uma PET WHHS is white opaque film with one side sealable layer with itself along with APET,C-PET, modified C-PET and A-PET coated boards. The film has high opacity and high whiteness index along with low transparency. Excellent flatness and good dimensional stability at elevated temperatures and exhibits good processability. APPLICATIONS Design for lidding in packaging applications and other industrial applications. Users don't need to coat any sealable coating during conversion.

General Information
Features	Good Dimensional Stability Good Processability
Uses	Film Industrial Applications Lids Pacifiers
Appearance	Opaque White
Forms	Film

Physical	Nominal Value	Unit	Test Method
Molding Shrinkage			ASTM D1204
Flow : 150°C, 30 min, 0.0300 mm	2.5	%
Flow : 150°C, 30 min, 0.0360 mm	2.5	%
Flow : 150°C, 30 min, 0.0500 mm	2.0	%
Across Flow : 150°C, 30 min, 2.30E-5 mm	0.60	%
Across Flow : 150°C, 30 min, 0.0300 mm	0.60	%
Across Flow : 150°C, 30 min, 0.0360 mm	0.60	%

Mechanical	Nominal Value	Test Method
Coefficient of Friction		ASTM D1894
vs. Itself - Dynamic ¹	0.45
vs. Itself - Dynamic ²	0.45
vs. Itself - Dynamic ³	0.45
vs. Itself - Static ⁴	0.55
vs. Itself - Static ⁵	0.55
vs. Itself - Static ⁶	0.55

Films	Nominal Value	Unit	Test Method
Film Thickness - Tested	30 36 50	µm
Film Thickness - Recommended / Available	30, 36, 50 µm
Tensile Strength			ASTM D882
MD : Break, 30 µm	137	MPa
MD : Break, 36 µm	137	MPa
MD : Break, 50 µm	137	MPa
TD : Break, 30 µm	147	MPa
TD : Break, 36 µm	147	MPa
TD : Break, 50 µm	147	MPa
Tensile Elongation			ASTM D882
MD : Break, 30 µm	130	%
MD : Break, 36 µm	130	%
MD : Break, 50 µm	130	%
TD : Break, 30 µm	80	%
TD : Break, 36 µm	80	%
TD : Break, 50 µm	80	%
Yield			Internal Method
30.0 µm	23.8	m²/kg
36.0 µm	19.8	m²/kg
50.0 µm	14.1	m²/kg

Additional Information	Nominal Value	Unit	Test Method
Seal Strength ⁷			Internal Method
140°C, 30.0 µm	984.3	g/2.5 cm
140°C, 36.0 µm	984.3	g/2.5 cm
140°C, 50.0 µm	984.3	g/2.5 cm
Wetting Tension - Plain side			ASTM D2578
30.0 µm	44	dyne/cm
36.0 µm	44	dyne/cm
50.0 µm	44	dyne/cm

Optical	Nominal Value	Unit	Test Method
Opacity			Internal Method
-- ⁸	85	%
-- ⁹	85	%
-- ¹⁰	85	%
Haze			ASTM D1003
30.0 µm	98	%
36.0 µm	98	%
50.0 µm	98	%

Note Message
1 .	50 µm
2 .	36 µm
3 .	30 µm
4 .	30 µm
5 .	36 µm
6 .	50 µm
7 .	Seal to seal surface, 2s, 3 kg/cm² pressure
8 .	50 µm
9 .	36 µm
10 .	30 µm

Resin Grade	Manufacturer	Category	Trademark
RABALON® MJ8301C	Mitsubishi Chemical Performance Polymers, Inc.	TPE	RABALON®
Zytel® FG70G30HSR2 BK309	DuPont Performance Polymers	Nylon 66	Zytel®
Fainplast PVC GS 54	Fainplast Compounds S.r.l	PVC, Unspecified	Fainplast PVC
Karina GRAY COLOR CONCENTRATE 18/15-FC-LMP	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina
StarFlex® 7025-1104	Star Thermoplastic Alloys & Rubbers, Inc.	TPE	StarFlex®

Category:	PET , Polyethylene Terephthalate
Manufacturer:	Ester Industries Ltd.
Trademark:	UmaPET
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	mVAZy0_UmaPET-WHHSO.pdf
PRICE:	Order Products email sales@su-jiao.com