LUVOTECH® MR 1025 BK Datasheet,Nylon 66,Lehmann & Voss & Co.-SHANGHAI SUSHENG

Message
LUVOTECH®MR 1025 BK is a polyamide 66 (nylon 66) material that contains a mineral filler. This product is available in Europe,. LUVOTECH®The main characteristics of MR 1025 BK are: anti-warping. Typical application areas include: textile/fiber engineering/industrial accessories Automotive Industry business/office supplies

General Information
Filler / Reinforcement	Mineral filler
Features	Low warpage
Uses	Textile applications Engineering accessories Application in Automobile Field Business equipment
Appearance	Black

Physical	Nominal Value	Unit	Test Method
Density	1.51	g/cm³	ISO 1183
Molding Shrinkage	0.60 - 1.2	%	DIN 16901

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	11000	MPa	ISO 527-2
Tensile Stress (Break)	110	MPa	ISO 527-2
Tensile Strain (Yield)	2.5	%	ISO 527-2
Flexural Modulus	9000	MPa	ISO 178
Flexural Stress	165	MPa	ISO 178
Coefficient of Friction
Dynamic	0.45
Static	0.40

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (23°C)	4.0	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength (23°C)	25	kJ/m²	ISO 179/1fU

Thermal	Nominal Value	Unit	Test Method
Continuous Use Temperature	120	°C	UL 746B
Maximum operating temperature- Short Term	140	°C
Vicat Softening Temperature	240	°C	ISO 306

Injection	Nominal Value	Unit
Drying Temperature
Hot air dryer, A	75.0	°C
Vacuum dryer, B	105	°C
Drying Time
Hot air dryer, A	6.0 - 16	hr
Vacuum dryer, B	4.0 - 6.0	hr
Suggested Max Moisture	0.10	%
Rear Temperature	290 - 310	°C
Middle Temperature	290 - 310	°C
Front Temperature	290 - 310	°C
Nozzle Temperature	280 - 300	°C
Processing (Melt) Temp	290	°C
Mold Temperature	90.0 - 120	°C

Injection instructions
General In general LUVOTECH® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.1%, otherwise molecular degradation and surface defects (e.g. smearing) may occur. Due to rapid absorption of water, originally sealed containers should only be opened immediately prior to processing. Excessively high predrying temperatures may cause discoloration. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Injection instructions

General In general LUVOTECH® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.1%, otherwise molecular degradation and surface defects (e.g. smearing) may occur. Due to rapid absorption of water, originally sealed containers should only be opened immediately prior to processing. Excessively high predrying temperatures may cause discoloration. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Category:	Nylon 66 , Polyamide 66
Manufacturer:	Lehmann & Voss & Co.
Trademark:	LUVOTECH®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	mV43UZ_LUVOTECH-MR-1025-BK.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Silopren® Electro 1800	Momentive Performance Materials Inc.	Rubber	Silopren®
SNOLEN® IM 31/54	JSC Gazprom neftekhim Salavat	HDPE	SNOLEN®
EPO-TEK® 353ND-T4	Epoxy Technology Inc.	Epoxy	EPO-TEK®
Hostacom X M3 T14 151237	LyondellBasell Industries	PP Copolymer	Hostacom
Durethan® BKV 230 DUS008 000000	LANXESS GmbH	Nylon 6	Durethan®