Hostalen PP H1022
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hostalen PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mUfrSm_Hostalen-PP-H1022.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Hostalen PP H1022 is a natural, basic stabilisation polypropylene blockcopolymer with high melt viscosity and excellent low-temperature impact strength. The material Hostalen PP H1022 has not been tested and therefore has not been certified for pressure applications. For further details about the suitable applications for this material please contact LyondellBasell. Hostalen PP H1022 is not intended for medical and pharmaceutical applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.901 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/5.0 kg | 0.50 | g/10 min | ISO 1133 |
| 230°C/2.16 kg | 0.30 | g/10 min | ISO 1133 |
| 230°C/5.0 kg | 1.3 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 3 sec) | 66 | ISO 868 | |
| Ball Indentation Hardness (H 132/30) | 50.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - Secant (23°C) | 1200 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, 23°C) | 25.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield, 23°C) | 10 | % | ISO 527-2/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 3.0 | kJ/m² | ISO 179 |
| 0°C | 7.0 | kJ/m² | ISO 179 |
| 23°C | 35 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 75.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 149 | °C | ISO 306/A50 |
| Melting Temperature (DSC) | 165 | °C | ISO 3146 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 200 - 280 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 200 - 230 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RapidVac™ VA-258 | Innovative Polymers, Inc. | TSU | RapidVac™ |
| UBE Nylon 7034 B | UBE Engineering Plastics, S.A. | Nylon 612 | UBE Nylon |
| CLEARTUF MAX | M&G Gruppo Mossi & Ghisolfi | PET | CLEARTUF |
| Formolene® LH5320 | Formosa Plastics Corporation, U.S.A. | HDPE | Formolene® |
| Karina WHITE PVC COMPOUND 651D10/1-C-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |