RTP VLF 82109 Datasheet,PEI,RTP Company-SHANGHAI SUSHENG

Message
"Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade."

General Information
Filler / Reinforcement	Long glass fiber, 50% filler by weight
RoHS Compliance	Contact manufacturer
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Density	1.68	g/cm³	ISO 1183
Moisture Content	0.020	%

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	17000	MPa	ISO 527-2
Tensile Stress	195	MPa	ISO 527-2
Tensile Strain (Yield)	1.0	%	ISO 527-2
Flexural Modulus	17000	MPa	ISO 178
Flexural Stress	290	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact ¹	20	kJ/m²	ISO 180/1A

Additional Information
All data listed is for natural or black colored materials. Pigments can affect properties.Desiccant Type Dryer Required.Additional Processing Details: Use a reverse barrel profile. To maximize fiber length, the following injection barrel, screw, and tip designs should be followed. L/D ratio 16/1 - 22/1, Compression ratio 2:1, Flight depth 5 mm minimum, in feed section, Screw diameter 16.5 - 20 mm minimum, Compression section length 12 - 13 diameters, Check ring valve assembly - free flow type no restrictions, Nozzle orifice 6 mm diameter. Feed throat from hopper to machine must have sufficient opening to prevent bridging of long pellet composition.

Additional Information

All data listed is for natural or black colored materials. Pigments can affect properties.Desiccant Type Dryer Required.Additional Processing Details: Use a reverse barrel profile. To maximize fiber length, the following injection barrel, screw, and tip designs should be followed. L/D ratio 16/1 - 22/1, Compression ratio 2:1, Flight depth 5 mm minimum, in feed section, Screw diameter 16.5 - 20 mm minimum, Compression section length 12 - 13 diameters, Check ring valve assembly - free flow type no restrictions, Nozzle orifice 6 mm diameter. Feed throat from hopper to machine must have sufficient opening to prevent bridging of long pellet composition.

Injection	Nominal Value	Unit
Drying Temperature - Desiccant Dryer	135	°C
Drying Time - Desiccant Dryer	4.0	hr
Dew Point	-30.0	°C
Processing (Melt) Temp	350 - 380	°C
Mold Temperature	120 - 160	°C
Injection Pressure	70.0 - 125	MPa

Note Message
1 .	4mm thickness

Resin Grade	Manufacturer	Category	Trademark
Microthene® F FA70000	LyondellBasell Industries	HDPE	Microthene® F
Sipolprene® 35195 W	SIPOL S.p.A	TPC-ET	Sipolprene®
Nypol® PA B3 G50 HS UV PRTA010 NT304	Petropol Industry and Trade of Polymers LTDA	Nylon 6	Nypol® PA
TECHNYL STAR® S 218 MT40 NATURAL	Solvay Engineering Plastics	Nylon 6	TECHNYL STAR®
CERTENE™ PRM-35C	Muehlstein	PP Random Copolymer	CERTENE™

Category:	PEI , Polyether Imide
Manufacturer:	RTP Company
Trademark:	RTP
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	mUUDE3_RTP-VLF-82109.pdf
PRICE:	Order Products email sales@su-jiao.com