Comtrex Flexible PVC® 71XCF
| Category: | PVC, Flexible , Flexible Polyvinyl Chloride |
| Manufacturer: | Mitsubishi Chemical Performance Polymers, Inc. |
| Trademark: | Comtrex Flexible PVC® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mTR4u6_Comtrex-Flexible-PVC-71XCF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
COMTREX FLEXIBLE PVC 71XCF is a Cadmium Free compound typically used in interior applications such as molding decorative covers for arm rest assemblies that require wear resistance. This compound is available in custom matched black and integral colors. Gloss level will depend on mold design and application. Designed to meet Daimler Chrysler Corporation Material Standard MS-DC526. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | 64 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Elongation (Break) | 350 | % | ASTM D638 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 12.8 | MPa | ASTM D412A |
| Tear Strength 2 | 38.7 | kN/m | ASTM D1004 |
| Thermal | Nominal Value | Test Method | |
|---|---|---|---|
| Cold Bend (-29°C, 2.50 cm) | Flexible, No Cracks | Internal Method |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| FMVSS Flammability | Self-Extinguishing (SE) | FMVSS 302 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Accelerated Weathering Duration 3 | No objectionable change in color or gloss. No objectionable defects. | SAE J1885 | |
| Fog Test | Very Slight Fog | Internal Method | |
| Hot/Cold Cycling - 24 hours | Internal Method | ||
| -29°C | No splitting, cracking, loss of appearance qualities, or physical properties | ||
| 79°C | No splitting, cracking, loss of appearance qualities, or physical properties | ||
| Volatile Loss - 72 hours (79°C) | 0.50 | % | Internal Method |
| Note Message | |
|---|---|
| 1 . | Die C, 500 mm/min |
| 2 . | 50 mm/min |
| 3 . | 600 kJ/m² exposure to Interior Xenon Arc Weather-ometer per SAE J1885. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shinko-Lac® ABS GH-8 | Mitsubishi Rayon America Inc. | ABS | Shinko-Lac® |
| Tecomid® NA40 MR15 NL IL | Eurotec Engineering Plastics | Nylon 66 | Tecomid® |
| Moplen HP525J | PolyMirae | PP Homopolymer | Moplen |
| Ultramid® 1503-2 NF2004 | BASF Corporation | Nylon 66 | Ultramid® |
| COSMOTHENE® EVA MA-10 | TPC, The Polyolefin Company (Singapore) Pte Ltd | LDPE | COSMOTHENE® EVA |