Romiloy® 5230 GF 20
| Category: | PBT+ASA , Polybutylene Terephthalate + ASA |
| Manufacturer: | ROMIRA GmbH |
| Trademark: | Romiloy® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mT5tKM_Romiloy-5230-GF-20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Romiloy®5230 GF 20 is a polybutylene terephthalate + ASA (PBT + ASA) material, and the filler is 20% glass fiber reinforced material. This product is available in Europe, and the processing method is injection molding. Romiloy®The main characteristics of 5230 GF 20 are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.41 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 40 | g/10 min | ISO 1133 |
| Molding Shrinkage (23°C) | 0.30 - 0.60 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 6450 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, 23°C) | 98.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 6.0 | % | ISO 527-2/5 |
| Flexural Modulus 1(23°C) | 5700 | MPa | ISO 178 |
| Flexural Stress 2(23°C) | 150 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 5.0 | kJ/m² | ISO 179/1eA |
| 23°C | 6.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 35 | kJ/m² | ISO 179/1eU |
| 23°C | 45 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 210 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Additional Information |
|---|
| The value listed as Molding Shrinkage ISO 294-4, was tested in accordance with DIN 16901. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 - 100 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.040 | % | |
| Suggested Max Regrind | 5 | % | |
| Rear Temperature | 240 - 260 | °C | |
| Middle Temperature | 240 - 260 | °C | |
| Front Temperature | 240 - 260 | °C | |
| Processing (Melt) Temp | < 260 | °C | |
| Mold Temperature | 75.0 - 100 | °C | |
| Injection Rate | Moderate | ||
| Back Pressure | < 1.00 | MPa | |
| Screw Speed | 12 - 18 | rpm |
| Injection instructions |
|---|
| Holding Pressure: moderate to high |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vydyne® R525H | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| Innoprene 1550N/B | Kumho Polychem Co., Ltd. | TPV | Innoprene |
| POLIMAXX BM3245PC | IRPC Public Company Limited | HDPE | POLIMAXX |
| OTECH ALLOY OM6018-Boot | OTECH Corporation | TP, Unspecified | OTECH ALLOY |
| Durethan® BKV 230 DUS008 000000 | LANXESS GmbH | Nylon 6 | Durethan® |