GAPEX® RPP30EA16NA
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Ferro Corporation |
| Trademark: | GAPEX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mT3x8e_GAPEX-RPP30EA16NA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
GAPEX®RPP30EA16NA is a polypropylene homopolymer (PP Homopoly) material, and its filler is 31% glass fiber reinforced material. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. The processing method is injection molding. GAPEX®The main features of the RPP30EA16NA are:
GAPEX®The typical application fields of RPP30EA16NA are: automobile industry |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.15 | g/cm³ | ASTM D792 |
| -- | 1.13 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 230°C/2.16 kg | 3.0 | g/10 min | ASTM D1238 |
| 230°C/2.16 kg | 3.5 | g/10 min | ISO 1133 |
| Molding Shrinkage | |||
| Flow | 0.40 | % | ASTM D955 |
| Vertical flow direction | 0.60 | % | ISO 294-4 |
| Flow direction | 0.60 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 75 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield | 82.7 | MPa | ASTM D638 |
| Yield, 23°C | 82.8 | MPa | ISO 527-2 |
| Tensile Elongation (Break) | 6.0 | % | ASTM D638 |
| Flexural Modulus | |||
| -- | 4210 | MPa | ASTM D790 |
| -- | 5200 | MPa | ISO 178 |
| Flexural Strength (Yield) | 117 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 85 | J/m | ASTM D256 |
| -40°C | 5.5 | kJ/m² | ISO 180 |
| 23°C | 8.0 | kJ/m² | ISO 180 |
| Unnotched Izod Impact (23°C) | 640 | J/m | ASTM D256 |
| Dart Drop Impact | 0.565 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 163 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 158 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 149 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 150 | °C | ISO 75-2/A |
| Additional Information |
|---|
| Tensile/Izod Change, 1,000 hrs @ 140°C, ISO 188: +10/-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 - 82.2 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 221 - 238 | °C | |
| Middle Temperature | 227 - 243 | °C | |
| Front Temperature | 232 - 260 | °C | |
| Nozzle Temperature | 232 - 260 | °C | |
| Processing (Melt) Temp | 221 - 238 | °C | |
| Mold Temperature | 37.8 - 65.6 | °C | |
| Injection Rate | Slow-Moderate | ||
| Back Pressure | 0.138 - 0.345 | MPa | |
| Cushion | 5.08 - 12.7 | mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Marvel™ M40 | SCG Chemicals Co., Ltd. | LLDPE | Marvel™ |
| SITRALIN 15E-TF10-HK-GF10 / C6PS | SITRAPLAS GmbH | ASA+Nylon | SITRALIN |
| Diakon® CMG314 | Lucite International Inc. | Acrylic (PMMA) | Diakon® |
| Sylvin 9604-95 Clear Black 2103 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 9077-88 Grey 9462 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |