KOPPS® S15G30HIBL
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Kolon Plastics, Inc. |
| Trademark: | KOPPS® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mRnZrr_KOPPSS15G30HIBL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| KOPPS®S15G30HIBL is a polyphenylene sulfide (PPS) product, which contains a 30% glass fiber reinforced material. It is available in North America, Latin America, Europe or Asia Pacific. The main characteristics are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.55 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Transverse flow | 1.2 | % | ISO 294-4 |
| Flow | 0.30 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 0.020 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 115 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (23°C) | 150 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 2.5 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 8200 | MPa | ISO 178 |
| Flexural Stress (23°C) | 230 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 14 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 260 | °C | ISO 75-2/A |
| Melting Temperature | 285 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 160 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.8 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature - Desiccant Dryer | 120 - 130 | °C | |
| Drying Time - Desiccant Dryer | 3.0 - 5.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 230 - 250 | °C | |
| Middle Temperature | 290 - 310 | °C | |
| Front Temperature | 290 - 310 | °C | |
| Nozzle Temperature | 300 - 320 | °C | |
| Mold Temperature | 120 - 140 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Makropol® PC A3 MF UV BRCA011 PC318 | Petropol Industry and Trade of Polymers LTDA | PC | Makropol® PC |
| NEXUS PC PC20NBR | Nexus Resin Group, LLC. | PC | NEXUS PC |
| Kumho ABS 775 | Korea Kumho Petrochemical Co., Ltd. | ABS | Kumho ABS |
| LNP™ THERMOCOMP™ QF008 compound | SABIC Innovative Plastics | Nylon 610 | LNP™ THERMOCOMP™ |
| Sylvin 8980-85 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |